The latest research progress on residual ultimate strength of metallic pipelines with structural damage is presented through literature survey. The investigated pipe diameter-to-thickness ratios majorly lie between 20 and 50, which are typically applicable in deep water. Influential parameters in terms of pipe load, installation process and material that affect the ultimate strength of pipes are categorised. Structural damage including dent, metal loss and crack is identified and efforts are made to summarise critical damage factors such as dent length and crack depth. Furthermore, research and prediction methods on pipe residual ultimate strength in terms of experimental tests, numerical simulations and analytical predictions are summarised and discussed. Specific details on how to introduce, simplify and simulate structural damage are presented and discussed. It is expected that the mechanism of residual ultimate strength of metallic pipes with structural damage can be clarified through this study so that guidance will be provided for researchers in this field.

A dent is one of the main structural damages that may affect ultimate strength. In this paper, the residual ultimate strength of dented metallic pipes subjected to a bending moment is quantitatively investigated. The numerical model is developed accounting for the variation of the dent length (l_d), dent depth (d_d), dent width (w_d), dent rotation angle (θ_d) and dent location based on ABAQUS Python. The numerical model is validated by test results from a four-point bending test. Subsequently, a parametric investigation is performed on the effects of wave-type initial imperfection, D/t and dent geometrical parameters. It is found that both l_d and d_d have a significant effect on the residual ultimate strength of dented metallic pipes, while the effect of w_d is slight. Finally, an empirical formula with respect to l_d and d_d has been proposed for the prediction of bending moment, which can be deployed for practical purposes.

The ultimate strength of metallic pipelines will be inevitably affected when they have suffered from structural damage after mechanical interference. The present experiments aim to investigate the residual ultimate bending strength of metallic pipes with structural damage based on large-scale pipe tests. Artificial damage, such as a dent, metal loss, a crack, and combinations thereof, is introduced to the pipe surface in advance. Four-point bending tests are performed to investigate the structural behavior of metallic pipes in terms of bending moment–curvature diagrams, failure modes, bending capacity, and critical bending curvatures. Test results show that the occurrence of structural damage on the pipe compression side reduces the bending capacity significantly. Only a slight effect has been observed for pipes with damage on the tensile side as long as no fracture failure appears. The possible causes that have introduced experimental errors are presented and discussed. The test data obtained in this paper can be used to further quantify damage effects on bending capacity of seamless pipes with similar D/t ratios. The comparison results in this paper can facilitate the structural integrity design as well as the maintenance of damaged pipes when mechanical interference happens during the service life of pipelines.