Metal–organic frameworks (MOFs) are porous materials assembled using metal and organic linkers, showing a high specific surface area and a tunable pore size. Large portions of metal open sites in MOFs can be exposed to electrolyte ions, meaning they have high potential to be used as electrode materials in energy storage devices such as supercapacitors. Also, they can be easily converted into porous metal oxides by heat treatment. In this study, we obtained high energy storage performance by preparing electrode materials through applying heat treatment to manganese MOFs (Mn-MOFs) under air. The chemical and structural properties of synthesized and thermally treated Mn-MOFs were measured by Fourier-transform infrared spectroscopy (FTIR), Raman spectroscopy, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). The surface area and porosity were investigated by nitrogen adsorption/desorption isotherms. The electrochemical properties were studied by cyclic voltammetry (CV) and galvanostatic charge–discharge (GCD) using a three-electrode cell. It was found that Mn-MOF electrodes that underwent heat treatment at 400 °C under air consisted of Mn₂O₃ with high specific surface area and porosity. They also showed a superior specific capacitance of 214.0 F g⁻¹ and an energy density value of 29.7 Wh kg⁻¹ (at 0.1 A g⁻¹) compared to non-treated Mn-MOFs.

MXenes consisting of thin layers of transition metal carbides or nitrides are good candidates for electrode materials due to their excellent electrical conductivity and fast ion transfer. Electrospun carbon nanofibers are highly porous and electrically conductive, making them attractive for electrode materials. In this study, free-standing electrodes were prepared by the dip-coating of carbon nanofibers (CNFs) in the MXene (Ti₃C₂) colloidal solution, which was synthesized via the wet-etching of MAX (Ti₃AlC₂) phase, and their chemical structures were investigated by X-ray diffraction and Fourier transform infrared spectroscopy. In addition, scanning and transmission electron microscopy were used to investigate the morphological and crystallographic features of MXene-coated CNFs. Surface area and pore volumes were investigated by nitrogen adsorption/desorption measurements. Supercapacitor performance was studied by assembling a 3-electrode system with 1M aqueous sodium sulfate solution as an electrolyte. MXene-coated CNFs exhibited a maximum specific capacitance of 514 F/g at 0.5 A/g, with energy and power densities of 71.4 Wh/kg at 0.5 A/g and 2.3 kW/kg at 5 A/g, respectively, which are relevantly higher compared to the pristine CNFs due to the pseudocapacitive behavior of MXenes. They also showed comparable cyclic stability during 5000 cycles with the CNFs. This result indicates that MXene-coated carbon nanofibers can be effective electrode materials for electrochemical energy storage.