Polypyrrole (PPy) is a conductive polymer known for its biocompatibility and ease of synthesis. Chemically polymerized PPy was synthesized in the presence of sodium dodecyl sulfate (SDS), showing correlations among chemical properties, physical morphology, and electrical properties. Focused synthesis parameters included the pyrrole (Py) concentration, SDS concentration, and ammonium persulfate (APS)/Py ratio. The addition of SDS during chemical polymerization influenced the physical morphology of PPy by altering the self-assembling process via micelle formation, yielding sheet-like morphologies. However, the phenomenon also relied heavily on other synthesis parameters. Varying SDS concentrations within the 0.01 to 0.30 M window produced PPy sheets with no significant difference in optical band gap or physical size. While using 0.10 M SDS, an increase in Py concentration from 0.10 to 0.30 M yielded a larger size of PPy as the morphology changed from sheet-like to irregular shape. The band gap dropped from 2.35 to 1.10 eV, and the conductivity rose from 6.80 × 10^-1 to 9.40 × 10^-1 S/m. With an increase in the APS/Py ratio, the PPy product changed from a random to a sheet-like form. The product provided a larger average size, a decreased band gap, and increased electrical conductivity. Py polymerization in the absence of SDS revealed no significant change in shape or size as the Py concentration increased from 0.10 to 0.30 M; only a sphere-like form was observed, with a large band gap and small conductivity. Results from Raman spectral analysis indicated a correlation between optical band gap, physical morphology, and bipolaron/polaron ratio, mainly at the wavelengths associated with C-C stretching and C-H deformation. The increase in average size was associated with a decrease in band gap and resistance as well as an increase in the bipolaron/polaron ratio. This work indicates a strong correlation between size, morphology, electrical properties, and the bipolaron/polaron ratio of PPy in the presence of SDS.

This research aims to deepen the understanding of the relationship between conductivity and morphology in polypyrrole (PPy) via a comparison of the bipolaron to polaron ratios with a focus on the C-H deformation area. PPy samples were synthesized with different surfactants: sodium dodecyl sulfate (SDS), cetyltrimethylammonium bromide (CTAB), and tween 80 (TW). This study revealed that SDS significantly altered the bipolaron and polaron in the C-H deformation region and showed higher conductivity than other surfactants. Notably, the morphological shifts to a sheet-like structure when using ammonium sulfate (APS) contrasted with the particle-like form observed with ferric chloride (FeCl₃). These results showed that if the oxidant changed, the bipolaron and polaron ratios in C-H deformation were unrelated to PPy morphology. However, this work showed a consistent relationship between SDS use, the bipolaron and polaron ratios in the C-H deformation, and the conductivity properties. Moreover, the natural positive charge of PPy and negatively charged SDS molecules may lead to an electrostatic interaction between PPy and SDS. This work assumes that this interaction might cause the transformation of polaron to bipolaron in the C–H deformation region, resulting in improved conductivity of PPy. This work offers more support for the future investigation of PPy characteristics.

This research aims to deepen the understanding of the relationship between conductivity and morphology in polypyrrole (PPy) via a comparison of the bipolaron to polaron ratios with a focus on the C-H deformation area. PPy samples were synthesized with different surfactants: sodium dodecyl sulfate (SDS), cetyltrimethylammonium bromide (CTAB), and tween 80 (TW). The study revealed that SDS significantly altered the bipolaron and polaron in C-H deformation region and showed higher conductivity than other surfactants. Notably, the morphological shifts to a sheet-like structure when using ammonium sulfate (APS) contrasted with the particle-like form observed with ferric chloride (FeCl3). These results showed that if the oxidant changed, the bi-polaron and polaron ratios in C-H deformation were unrelated to PPy morphology. However, this work showed a consistent relationship between SDS use, the bipolaron and polaron ratios in the C-H deformation, and the conductivity properties. Moreover, the natural positive charge of PPy and negatively charged SDS molecules may lead to an electrostatic interaction between PPy and SDS. This work assumes that this interaction might cause the transformation of polaron to bipolaron in the C-H deformation region, resulting in improved conductivity of PPy. This work offers more support for the future investigation of PPy characteristics.