Fullerenols are nanosized water-soluble polyhydroxylated derivatives of fullerenes, specific allotropic form of carbon, bioactive compounds and perspective pharmaceutical agents. Antioxidant activity of fullerenols was studied in model solutions of organic and inorganic toxicants of oxidative type - 1,4-benzoquinone and potassium ferricyanide. Two fullerenol preparations were tested: С60О2-4(ОН)20-24 and mixture of two types of fullerenols С60О2-4(ОН)20-24+С70О2-4(ОН)20-24. Bacteria-based and enzyme-based bioluminescent assays were used to evaluate a decrease in cellular and biochemical toxicities, respectively. Additionally, the enzyme-based assay was used for the direct monitoring of efficiency of the oxidative enzymatic processes. The bacteria-based and enzyme-based assays showed similar peculiarities of the detoxification processes: (1) ultralow concentrations of fullerenols were active (ca 10-17-10-4 and 10-17-10-5 g/L, respectively), (2) no monotonic dependence of detoxification efficiency on fullerenol concentrations was observed, and (3) detoxification of organic oxidizer solutions was more effective than that of the inorganic oxidizer. The antioxidant effect of highly diluted fullerenol solutions on bacterial cells was attributed to hormesis phenomenon; the detoxification was concerned with stimulation of adaptive cellular response under low-dose exposures. Sequence analysis of 16S ribosomal RNA was carried out; it did not reveal mutations in bacterial DNA. The suggestion was made that hydrophobic membrane-dependent processes are involved to the detoxifying mechanism. Catalytic activity of fullerenol (10-8 g/L) in NADH-dependent enzymatic reactions was demonstrated and supposed to contribute to adaptive bacterial response.

In this paper, we study the possibility of obtaining iron and titanium-vanadium concentrates with highest contents of iron and titanium, respectively, through hydrometallurgical processing of the titanomagnetite ores of the Chineisk deposit. We varied two key parameters to determine the efficiency of the process: (a) concentration of leaching solution (ammonium fluoride); and (b) acidity of solution. Ammonium fluoride concentration was varied from 0.08 mol/L to 4.2 mol/L with the other fixed parameters. It was shown that optimum ammonium fluoride concentration for leaching the ore is 0.42 mol/L; at these concentrations iron and titanium contents are about 62.8 wt % and 3.5 wt % in solid phase, respectively. The acidity of solution was changed by adding of hydrofluoric acid with varied concentration (from 0.86 mol/L to 4.07 mol/L) to ammonium fluoride solution with fixed concentration of 0.42 mol/L. The best results (degree of titanium extraction = 63.7%) were obtained when using a solution of hydrofluoric acid with concentration 4.07 mol/L. In this case, the addition of acid makes it possible to increase the Fe/Ti ratio by 3.4 times in comparison with the original ore. Thus, we conclude that acidity and the concentration of ammonium fluoride solution significantly influences the selectivity of the hydrometallurgical process.