Mesophase pitch is usually prepared by radical polymerization or catalytic polymerization from coal tar, petroleum, and aromatic compounds, and the catalytic synthesis of mesophase pitch from pure aromatic compounds is more controllable in the preparation of high-quality mesophase pitch. However, the corrosive and highly toxic nature of the catalyst has limited the further development of this method. In this study, mesophase pitch was synthetized using ethylene tar and naphthalene as raw materials and boron trifluoride diethyl etherate as a catalyst. The effect of the catalytic reaction on the structure and properties of the mesophase pitch was investigated. The results show that naphthalene plays an important role in the mesophase content and reaction pressure (from above 6 MPa to 2.35 MPa). Mesophase pitch with fine-flow texture can be prepared by introducing more methylene groups, naphthenic structures, and aliphatic hydrocarbons during synthesis. Carbon fibers prepared from mesophase pitch show a split structure, and the thermal conductivity is 730 W/(m·K). This work provides theoretical support for lower toxicity and causticity and for reaction-controlled technology for the synthesis of high-purity mesophase pitch.

A polarized light microscope (PLM) was utilized to examine the optical textures of mesophase pitch (MP) and MP-derived fibers, which aimed to reveal the arrangement and orientation characteristics of pitch molecules and to clarify the evolution and transformation mechanism of carbonaceous microcrystalline from pitch fibers to graphitized fibers. The results found that there were distinct optical textures in MP, where one side exhibited a transition from a flattening plane to a mountain-like undulating plane. This transition corresponded to the arrangement of pitch molecules, resembling stacked lamellar structures reminiscent of curved paper. Meanwhile, the optical textures of fibers revealed that the blue substance was wrapped around the red grain-like domains in the longitudinal section and confirmed that the red part belonged to the pyridine insoluble fraction of MP and the blue part belonged to its pyridine-soluble fraction. After graphitization, the red part was transformed into graphite sheets and the blue part was transformed into an amorphous carbon layer which was wrapped around the graphite sheets, forming a carbonaceous microcrystalline package-like bag. Therefore, this study provided a comprehensive interpretation of the structural evolution mechanism of MP and MP-derived fibers based on their macro-optical textures and micro-nanostructures.