Liquid epoxy resins have received much attention from both academia and the chemical industry as eco-friendly volatile organic compound (VOC)-free alternatives for applications in coatings and adhesives, especially in those used in households. Epoxy resins show high chemical resistance and high creep resistance. However, due to their brittleness and lack of thermal stability, additional fillers are needed for improving the mechanical and thermal properties. Halloysite nanotubes (HNTs) are naturally abundant, inexpensive, and eco-friendly clay minerals that are known to improve the mechanical and thermal properties of epoxy composites after suitable surface modification. Zirconium is well known for its high resistance to heat and wear. In this work, zirconium oxide-impregnated HNTs (Zr/HNTs) were added to epoxy resins to obtain epoxy composites with improved mechanical and thermal properties. Zr/HNTs were characterized by field-emission transmission electron microscopy, transmission electron microscopy with energy-dispersive X-ray spectroscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. Changes in the thermal properties of the epoxy composites were characterized by thermo mechanical analysis and differential scanning calorimetry. Furthermore, flexural properties of the composites were analyzed using a universal testing machine.

The graphite block as a phase change materials (PCMs) was manufactured by graphitization of a carbon block. Carbon blocks were prepared by filler (cokes or graphite) and binder (pitch). The binder-coated filler was thermally treated for carbonization. The gases generated from the evaporation of low molecular weight components in the binder pitch during the carbonization process were not released to the outside. Consequently, porosity and volume expansion were increased in artificial graphite, and thereby the thermal conductivity decreased. In this study, to prevent the decrease of thermal conductivity in the artificial graphite due to the disadvantages of binder pitch, the carbon block was prepared by the addition of carbon black, which can absorb low molecular weight compounds and release the generated gas. The properties of the prepared carbon blocks were analyzed by SEM, TGA, and thermal conductivity. The addition of carbon black (CB) decreased the porosity and volume expansion of the carbon blocks by 38.3% and 65.9%, respectively, and increased the thermal conductivity by 57.1%. The CB absorbed the low molecular weight compounds of binder pitch and induced the release of generated gases during the carbonization process to decrease porosity, and the thermal conductivity of the carbon block increased.