Chitosan nanoparticles (CS-NPs) are currently under investigation for a wide range of applications in nanomedicine. We investigated the structural, morphological, and molecular properties of CS-NPs synthesized via ionic gelation and designed specifically for drug delivery. The CS-NPs were prepared at concentrations ranging from 0.25 to 1.0% w/v. The 1.0% w/v CS-NPs were also functionalized with polyethylene oxide (PEO) alone and with a diblock copolymer of PEO and polypropylene glycol (PPG). The average nanoparticle size determined from TEM imaging is in the 11.3 to 14.8 nm range. The XRD and TEM analyses reveal a semi-crystalline structure with a degree of crystallinity dependent upon the nature of CS-NP functionalization. Functionalizing with PEO had no effect, whereas functionalizing with PEO-PPG resulted in a significant increase in the crystallinity of the 1.0% w/v CS-NPs. Additionally, the CS/TPP concentration (CS:TPP fixed at a 1:1 ratio) did not impact the degree of crystallinity of the CS-NPs. FTIR analysis confirmed the incorporation of TPP with CS and an increase in hydrogen bonding in more crystalline CS-NPs.

Chitosan (CS) nanoparticles are under investigation for a wide range of applications in nanomedicine. The structural, molecular and physicochemical properties of chitosan nanoparticles have a direct bearing on their efficacy in drug conjugation and delivery, gene delivery, and tissue engineering. Herein we report on the structural, morphological and molecular properties of chitosan nanoparticles synthesized using the ionic gelation method with the intended purpose of being used for drug delivery. The chitosan nanoparticles (CS-NPs) were prepared in the 0.25 to 1.0% w/v concentration range, whereas separate samples of the 1.0% w/v CS-NPs were also functionalized with polyethylene oxide (PEO) alone and with a diblock copolymer of PEO and polypropylene glycol (PPG). The average size of the CS-NPs was determined from TEM imaging to be in the range of 11.3 to 14.8 nm. The XRD and TEM analyses show that the CS-NPs have semi-crystalline structure with the degree of crystallinity depending upon the nature of synthesis. Our results show that functionalizing the 1.0% w/v CS-NPs with PEO increases the degree of crystallinity whereas functionalizing with the diblock copolymer PEO - PPG results in a significant increase in their degree crystallinity. The CS/TPP concentration (CS:TPP fixed at 1:1 ratio) had no apparent effect on the degree of crystallinity of the CS-NPs. The results from the FTIR analysis confirm incorporation of TPP with CS in the CS-NPs. Additionally, FTIR analysis shows an enhancement of hydrogen bonding that is consistent with the increase in the degree of crystallinity of the CS-NPs.