In the last years, the excessive use of plastic and other synthetic materials, that are generally difficult to dispose of, has caused growing ecological worries. These are contributing to redirecting the world’s attention to sustainable materials and a circular economy (CE) approach using recycling routes. In this work, bio-filaments for the Fused Filament Fabrication (FFF) 3D printing technique were produced from recycled polylactic acid (PLA) and artisanal ceramic waste by an extrusion process and fully characterized from a physical, thermal, and mechanical point of view. The data showed different morphological, thermal, rheological, and mechanical properties of the two produced filaments. Furthermore, the 3D objects produced from the 100% recycled PLA filament showed lower mechanical performance. However, the results have demonstrated that all the produced filaments can be used in a low-cost FFF commercial printer that has been modified with simple hand-made operations in order to produce 3D-printed models. The main objective of this work is to propose an example of easy and low-cost application of 3D printing that involves operations such as the reprocessing and the recyclability of materials, that are also not perfectly mechanically performing but can still provide environmental and economic benefits.

In this study, novel biocomposite filaments incorporating cocoa bean shell waste (CBSW) and poly(lactic acid) (PLA) were formulated for application in Fused Filament Fabrication (FFF) technology. CBSW, obtained from discarded chocolate processing remnants, was blended with PLA at concentrations of 5 and 10 wt.% to address the challenge of waste material disposal while offering eco-friendly composite biofilaments for FFF, thereby promoting resource conservation and supporting circular economy initiatives. A comprehensive analysis encompassing structural, morphological, thermal, and mechanical assessments of both raw materials and resultant products (filaments and 3D printed bars) was conducted. The findings reveal the presence of filler aggregates only in high concentrations of CBSW. However, no significant morphological or thermal changes were observed at either CBSW concentration (5 wt.% and 10 wt.%) and satisfactory printability was achieved. In addition, tensile tests on the 3D printed objects showed improved stiffness and load resistance in these samples at the highest CBSW concentrations. In addition, to demonstrate their practical application, several 3D prototypes (chocolate-shaped objects) were printed for presentation in the company’s shop window as a chocolate alternative; while retaining the sensory properties of the original cocoa, the mechanical properties were improved compared to the base raw material. Future research will focus on evaluating indicators relevant to the preservation of the biocomposite’s sensory properties and longevity.

Poly(lactic acid) (PLA) is one of the most widely used thermoplastic materials for 3D printing, particularly in the Fused Filament Fabrication technique. However, the printing process generates waste products and even though PLA is compostable, the possibility of recycling it provides ecological and economical benefits. In this work, a study on the stabilization of recycled PLA using charcoal (CC) was carried out, with the aim of overcoming the well-known problem of degradation (reduction in molecular weight) of PLA, during remelting. Microscopic investigations showed good dispersion of the filler in the polymer matrix, as well as better adhesion between the printed layers. Thermal analyses (Differential scanning calorimetry and thermogravimetry) indicate a stabilization of PLA waste because of the addition of small concentrations of CC to the recycled polymer matrix. These data are confirmed by GPC analyses, which show that the addition of filler is associated with higher molecular weight. Mechanical analysis indicated improved elongation at break and elasticity. Finally, a key ring was printed as an example of the better printability of the filament containing CC. The results indicate that a stabilization of the recycled PLA with a very low concentration of CC has been achieved. Improved 3D printability and properties of the 3D printed objects can be attained through recycling and recovery of wasted PLA, according to sustainability and circular economy matters.

The excessive use of materials that are generally difficult to discard, such as stone materials, has caused growing ecological concern. Among these, marble is extracted from quarries, but when the raw material is exhausted, these places are deserted. For this reason, several measures have been adopted in recent years to requalify these areas. In addition, recent technological developments involve the creation of innovative green materials that privilege the circular economy and waste recycling. This research presents the development of innovative, sustainable filaments for the fused filament fabrication (FFF) printing technique from recycled marble waste (MW) and biocompostable and biodegradable polylactic acid (PLA) matrix. MW was added to the polymer in concentrations of 10 wt.%, 20 wt.%, and 30 wt.%, and the blends were extruded to develop innovative green filaments. The chemical/structural properties of the raw materials and the thermal and mechanical features of the new composites were investigated. Composites containing 10 and 20 wt.% of MW showed good printability. In contrast, extrusion and printing difficulties were observed with 30 wt.% of MW. Finally, this paper proposes a project to renaturalize and requalify a disused marble quarry located in Trani (Apulia, Italy) with 3D printing devices using the newly produced eco-filaments, which have better features. The main purpose of this article is to propose a concrete, economic, and sustainable application of 3D printing involving processes such as waste and by-product recycling and renaturalization of disused quarries, with both economic and environmental benefits.