The cement industry, a key player in globalization and urbanization, has replaced traditional shelters with modern buildings, raising environmental concerns. This study examines the use of cement in construction in Togo, its impact on residents’ thermal comfort, and adaptation strategies for sustainable construction and well-being. The research was conducted in Lomé, Atakpamé, and Kara through documentary research, photography, household surveys, interviews, and temperature recordings, involving 646 households and nine interviews. Findings reveal a high use of cement due to availability, ease of use, strength, affordability, and aesthetics. Cement houses are generally less comfortable than earthen houses, particularly in hot climates. Lomé and Kara experience higher discomfort, while Atakpamé has lower discomfort despite cement dominance. Thermal comfort varies more during the day. Residents adopt strategies like sleeping outside, wearing light clothing, installing awnings and false ceilings, planting trees, staying hydrated, taking cool showers, and ventilating rooms.

In response to the challenges of climate change, this study explores the use of moringa pod powder as reinforcement in the manufacture of compressed earth bricks to promote sustainable building materials. The objective is to evaluate the impact of African locust bean pod powder on the mechanical properties of the bricks. Two types of soils from Togo were characterized according to geotechnical standards. Mixtures containing 8% African locust bean pod powder at various particle sizes (0.08 mm, 2 mm, and between 2 and 5 mm) were formulated and tested for compression and tensile strength. The results show that the addition of African locust bean pod reduces the mechanical strength of the bricks compared to the control sample without pods, with strengths ranging from 0.697 to 0.767 MPa, compared to 0.967 to 1.060 MPa for the control. However, the best performances for the mixtures were obtained with a fineness of less than 2 mm. This decrease in performance is attributed to several factors, including inadequate water content and suboptimal preparation and compaction methods. Optimizing formulation parameters is necessary to maximize the effectiveness of African locust bean pods. This work highlights the valorization of agro-industrial waste, paving the way for a better understanding of bio-based materials and future research for sustainable construction.

Faced with environmental challenges posed by traditional building materials and the management of agricultural waste, this study uses dwarf hulls, an abundant waste product in West Africa, as a natural stabilizer for earth bricks. Three mixtures were studied: soil + water (reference), soil + néré husk decoction, and soil + decoction with weekly sprinkling. The results show a significant improvement in compressive strength with the decoction. At 28 days, it increases from 0.967 MPa (reference) to 1.251 MPa with decoction and 1.360 MPa with sprinkling. At 90 days, these values reach 1.060 MPa, 1.39 MPa, and 1.502 MPa, respectively, confirming the beneficial effect of tannins and humidification. On the other hand, the tensile strength decreased from 0.10 MPa for the reference mixture to 0.08 MPa and 0.08 MPa with decoction and sprinkling. This study highlights the potential of using néré husk as a durable stabilizer. However, further research is needed, particularly on the addition of plant fibers, to improve tensile strength.

Integrating local, bio-sourced materials, such as earth and agricultural waste like dwarf hulls, is a sustainable solution to the challenges of climate change and increasing urbanization. The use of bio-based materials such as néré husk (Parkia biglobosa) in the manufacture of compressed earth bricks is a sustainable alternative for improving their thermal performance. This study assesses the impact of adding hulls in different forms (fine powder < 0.08 mm, aggregates from 2 mm to 5 mm, and aqueous maceration) on the thermal conductivity and effusivity of bricks. The tests were carried out using the asymmetric hot plane method, applying a constant heat flux and measuring the temperature variation via a thermocouple. Three samples of each formulation were analyzed to ensure the reliability of the results. The results show that the addition of fine powdered husk reduces the thermal conductivity of the bricks to 0.404 W/m.K and their effusivity to 922.2 W/(Km²) s¹/², compared with 0.557 W/m.K and 1000.32 W/(Km²) s¹/² for the control bricks. The addition of coarser aggregates (2 mm–5 mm) gives intermediate values (0.467 W/m.K and 907.99 W/(Km²) s¹/²). Aqueous maceration, on the other hand, results in an increase in thermal conductivity to 0.614 W/m.K. These results confirm that the shape and method of incorporation of the husk influence the thermal performance of the bricks, with fine powder offering the best thermal insulation. This approach highlights the potential of bio-based materials for eco-responsible construction.