This paper reports on the design and construction of a lightweight glass fiber-reinforced polymer roof structure in Basel, Switzerland. The sandwich construction allowed for an integration of static, building physical and architectural functions that enabled the prefabrication of the entire roof in only four lightweight elements that were easily transported to the site and rapidly installed. Cutting of foam blocks with a computerized numerical control machine and adhesive bonding proved to be advantageous procedures for the fabrication of the complex roof shape, without the use of expensive molds. The factor of safety of the design was adjusted during the design process through experimental verification. Although some of the characteristic material properties were overestimated in the preliminary design, the design properties for the final design were higher than for the preliminary design as it was possible to reduce the resistance factors (according to Eurocode format) after testing by a factor of 2.0. ...

In the summer of 2005, after eight years of use as a temporary bridge during the winter, the Pontresina Bridge for pedestrians was transported to the Swiss Federal Institute of Technology Lausanne for a detailed assessment of the structural safety, serviceability, and long-term durability of the bridge. The assessment included a visual inspection, quasistatic testing identical to that performed in 1997, and detailed investigations of material degradation. The visual inspection showed a variety of different local defects and damage such as local crushing caused by impact, local cracks due to inappropriate storage and lifting of the structure, fiber blooming, degradation of cut surfaces, and damage due to vandalism. Comparisons between load tests performed in 1997 and 2005 showed, however, that the structural safety and serviceability of the bridge have not been affected by these local damages. The stiffness of the pultruded shapes remained unchanged, whereas a slight decrease in strength between 13 and 18%...