With the rise of global industrialization, the requirements for the operating speed and carrying capacity of high-speed trains are increasingly higher. Because the wear and tear of rails gradually increases during the running of high-speed trains, strengthening or repairing rail surfaces is of paramount significance. Laser-directed energy deposition (DED) exhibits significant advantages in improving surface hardness, corrosion resistance, and abrasion resistance. Because of the multiple interacting optimization objectives, the development of a multi-objective optimization method for process parameters is significant for improving DED deposition quality. Response surface design employs multivariate quadratic regression equations to fit the functional relationship between the factors and the responses, which can be employed to find the optimal process parameters and solve multivariate problems. This study develops a multi-objective optimization model with response surface design and 2D process mappings to visually analyze the effects of scanning speed, laser power, and powder feed rate on aspect ratio, dilution rate, and microhardness. The optimal combination of process parameters for Ni-based alloys on U71Mn rail is a laser power of 431 W, a scanning speed of 5.34 mm/s, and a powder feed rate of 1.03 r/min. In addition, a multi-physics field finite element model is developed to analyze the evolution mechanism of the microstructure from the bottom to the top of the single track. This study can provide theoretical and technical support for the surface strengthening or repair of U71Mn rail.

In recent years, laser cladding technology has been widely used in surface modification of titanium alloys. To improve the wear resistance of titanium alloys, ceramic-reinforced nickel-based composite coatings were prepared on a TC4 alloy substrateusing coaxial powder feeding laser cladding technology. Ti (C, N) ceramic was synthesized in situ by laser cladding by adding different contents (10%, 20%, 30%, and 40%) of TiN, pure Ti powder, graphite, and In625 powder. Thisestudy showed that small TiN particles were decomposed and directly formed the Ti (C, N) phase, while large TiN particles were not completely decomposed. The in situ synthetic TiC_xN_1−x phase was formed around the large TiN particles. With the increase in the proportion of powder addition, the wear volume of the coating shows a decreasing trend, and the wear resistance of the surface coating is improving. The friction coefficient of the sample with 40% TiN, pure Ti powder, and graphite powder is 0.829 times that of the substrate. The wear volume is 0.145 times that of the substrate. The reason for this is that with the increase in TiN, Ti, and graphite in the powder, there are more ceramic phases in the cladding layer, and the hard phases such as TiC, Ti(C, N) and Ti2Ni play the role in the structure of the “backbone”, inhibit the damage caused by micro-cutting, and impede the movement of the tearing point of incision, so that the coating has a higher abrasion resistance.

Ultra-precision machining has higher requirements for the performance of abrasive tools, but the traditional grinding wheel has some problems such as irregular grain arrangement, limited chip space, and high grinding temperature. Therefore, a structured grinding wheel suitable for ultra-precision machining is proposed. In this study, the laser cladding method and ultrasonic vibration technology were combined to study the preparation process of a structured grinding wheel. Firstly, the quality evaluation system of the printing layer was established, and the shape coefficient and dilution rate were used to evaluate the laser cladding quality. The effects of laser power, sweep speed, powder feeding speed, and ultrasonic power on the shape coefficient and dilution rate of the printing layer were analyzed by single-factor experiments. The level range of each factor in the orthogonal experiment was established to optimize the process parameters. The surface morphology was observed, and the influence of ultrasonic vibration on the morphology was analyzed. The structured grinding wheel was prepared according to the optimized parameters.