Understanding the tribological properties of alloy-based sliding electrical contacts is crucial for both fundamental research and practical applications. Here, to explore the friction, wear, and contact resistance of a AgCuNi alloy/Au-electroplated layer during sliding, a ball-on-disk tribometer was coupled with a source meter. The experiments were conducted under various conditions including a current ranging from 0 to 1.0 A, a normal load ranging from 0.5 to 3.0 N, and a sliding speed of 40 mm/s. The results indicate that the wear of the friction pair is aggravated by both the current and the increase in the normal load. When the current was 0.5 A, the wear loss reached its lowest point. However, as the current increased from 0.5 A to 1.0 A, there was an intensification in Ag transfer from the alloy ball to the Au-electroplated layer, resulting in an increase in wear loss. Both the normal load and current have significant effects on both friction coefficient and contact resistance. The variation in contact resistance over time follows a similar pattern to that of the friction coefficient over time. The formation of a transfer film plays a crucial role in determining contact resistance, wear resistance, and friction coefficient. The experiment demonstrates that optimizing the normal load and current can adjust both the contact resistance and friction coefficient, thereby prolonging service life and ensuring the stability of contacts.

To avoid wear and tear of the slip ring due to electrical corrosion, the slip ring needs to undergo the running-in process under atmospheric conditions without current after assembly. To address the urgent demand for long-service capability space conductive slip rings in the aerospace field, the running-in behavior and failure mechanism between the AgCuNi alloy and Au-electroplated layer are investigated using a ball-on-disc tribometer in this paper. The results show that the transfer film composed of Au plays an important role in modifying the friction during the sliding process. With the accumulation of wear debris composed of Ag on the disc, the contact material of the friction pair changed from Au and Au to Au, Ag and Au, so the surface roughness of wear tracks increased. Finally, the transfer film broke, which made the layer fail. This paper reveals the key element failure mechanism that causes transfer film failure in the running-in contact area, which is used to reveal the friction behavior and failure mechanism of slip ring friction pair materials, and provides a basis for the selection of running-in parameters during the running-in process of slip rings before power-on operation.