MCrAlY (M = Ni and/or Co) metallic coatings are essential for the protection of hot-end components against thermal and corrosion damage. Increasing the Al content is considered a feasible solution to improve the high-temperature performance of MCrAlY coatings. In this paper, the effects of high Al contents (12–20 wt.%) on the phase constituents and cast microstructures in MCrAlY alloys were studied by high-energy X-ray diffraction and electron microscopy techniques combined with phase equilibria calculations. High Al content improved the stability of β, σ, and α phases. Meanwhile, an evolution of the cast microstructure morphology from a dendrite structure to an equiaxed grain structure was observed. The thermal properties were analyzed, which were closely related to the phase constituents and solid-to-solid phase transitions at evaluated temperatures. This work is instructive for developing high-Al-content MCrAlY coatings for next-generation thermal barrier applications.

Ti–Ta impedance-graded coatings were prepared using cold spraying combined with hot isostatic pressing. Compared to the general Ti–Ta binary diffusion couple, the interdiffusion coefficient of as-sprayed Ti–Ta can be increased by approximately 25 times at 1100 °C due to grain refinement at the interface of the cold-sprayed particles. By the control of interdiffusion, pure Ta and pure Ti regions can remain in the materials after hot isostatic pressing at 900 °C. Hot isostatic pressing with capsulate reduced the porosity of the material efficiently to less than 0.02%. The strength of the as-sprayed Ti–Ta composite coating was significantly improved to 990.1 MPa, and the fracture strain reached 11.5%. The strengthening mechanism of Ti–Ta composite coatings relies primarily on the hindrance of dislocation slip by phase interfaces between α and β. Moreover, the macroscopic interfacial bonding strength of the graded material exceeds 881 MPa, which is comparable to that of bulk materials.

The Al-Ta energetic structural material (ESM) has significant potential for applications in energetic fragments. To rationally design the hot isostatic pressing (HIP) process for Al-Ta, this paper developed a novel parameter identification method for the modified Drucker–Prager Cap (DPC) model. The identified parameters were subsequently applied to simulate the densification behavior of Al/Ta mixed powders during HIP. Based on the simulation results, the HIP process parameters for fabricating the Al-Ta ESM were determined. Meanwhile, the microstructure, mechanical properties, and impact-induced reaction characteristics of the HIP-fabricated Al-Ta ESM were further analyzed. The main results are as follows. The comparison between the HIP simulations and experiments revealed good agreement, confirming the high accuracy of the identification of the modified DPC model parameters. In addition, the Al-Ta ESM fabricated via HIP at 460 °C/140 MPa/2 h exhibits a dense microstructure and enhanced mechanical properties. Furthermore, it demonstrates effective damage performance during the penetration of double-layered targets.