The effect of alcaline and hot water surface treatments of piassava Attalea funifera fibers was investigated. The efficiency of each treatment was evaluated by Fourier transform infrared spectroscopy, X-ray diffractometry, optical microscopy, scanning electron microscopy and atomic force microscopy. The alkaline treatments were effective in removing the superficial lignin layer from the fiber, while the hot water treatment was not. Treatment with hot water and NaOH caused fiber defibrillation. NaOH was most effective in promoting both, a decrease in fiber diameter and an increase in fiber surface area. Treatment with Ca(OH)₂ led to the formation of a CaCO₃ layer deposited on the fiber, preventing defibrillation. The crystalline structure of the fiber was not altered by any of the treatments, maintaining type I cellulose.

For the purpose of renewable materials applications, Curauá fiber treated with 5% sodium hydroxide was added to high-density biopolyethylene, using an entirely Brazilian raw material of sugarcane ethanol. Polyethylene grafted with maleic anhydride was used as a compatibilizer. With the addition of curauá fiber, the crystallinity was reduced, possibly due to interactions in the crystalline matrix. A positive thermal resistance effect was observed for the maximum degradation temperatures of the biocomposites. When curauá fiber was added (5% by weight), the morphology showed interfacial adhesion, greater energy storage and damping capacity. Although curauá fiber additions did not affect the yield strength of high-density bio polyethylene, its fracture toughness improved. With the addition of curauá fiber (5% by weight), the fracture strain was greatly reduced to about 52%, the impact strength was also reduced, suggesting a reinforcing effect. Concomitantly, the modulus and the maximum bending stress, as well as the Shore D hardness of the curauá fiber biocomposites (at 3 and 5% by weight), were improved. Two important aspects of product viability were achieved. First, there was no change in processability and, second, with the addition of small amounts of curauá fiber, there was a gain in the specific properties of the biopolymer. The resulting synergies can help ensure more sustainable and environmentally friendly manufacturing of automotive products.