Water electrolysis is regarded as one of the most viable technologies for the generation of green hydrogen. Nevertheless, the anodic oxygen evolution reaction (OER) constitutes a substantial obstacle to the large-scale deployment of this technology, due to the considerable overpotential resulting from the retardation kinetics associated with the OER. The development of low-cost, high-activity, and long-lasting OER catalysts has emerged as a pivotal research area. Layered double hydroxides (LDHs) have garnered significant attention due to their suitability for use with base metals, which are cost-effective and exhibit enhanced activity. However, the current performance of LDHs OER catalysts is still far from meeting the demands of industrial applications, particularly in terms of their long-term stability. In this review, we provide an overview of the causes for the deactivation of LDHs OER catalysts and present an analysis of the various mechanisms employed to improve the stability of these catalysts, including the synthesis of LDH ultrathin nanosheets, adjustment of components and doping, dissolution and redeposition, defect creation and corrosion, and utilization of advanced carbon materials.

Electrooxidation of pollutants at potentials near or below the thermodynamic hydrogen evolution potential offers transformative opportunities for energy-efficient pollutant valorization and diverse energy devices. However, existing catalysts suffer from rapid deactivation due to the inevitable overoxidation. Herein, we present an amorphous phosphorus-doped CoFe₂O₄ catalyst that achieves industrial-level current densities (1 A cm⁻²) at ultralow potentials (0.06, 0.65, and -0.17 V vs. reversible hydrogen electrode) for hydrazine, sulfion, and borohydride electrooxidation, respectively, along with 400-hour stability at 300 mA cm⁻² in a hydrazine-assisted electrolyzer. Mechanistic studies reveal electron transfer from Co-P ligands to Co-O ligands, which enhances the involvement of Co-O ligands in low-potential electrooxidation while protecting Co-P ligands from overoxidation. Furthermore, more positive charges on Co centers lower the activation barrier for such pollutant electrooxidation. This work opens a paradigm for designing robust electrocatalysts by decoupling catalytic activity from oxidative deactivation.

Atomically dispersed metal–nitrogen–carbon (M-N-C) catalysts are regarded as ideal catalytic materials for the oxygen reduction reaction (ORR) under alkaline conditions. Compared with other ORR catalysts, M-N-C catalysts exhibit notable advantages, including low cost, high atomic utilization efficiency, and considerable catalytic potential. We provide a systematic review of recent research advances in enhancing the ORR performance of M-N-C catalysts, focusing on catalytic activity and stability. First, the reaction mechanism of the ORR on the surfaces of the M-N-C catalysts is elucidated. Second, the primary strategies employed in recent years to improve their catalytic activity and stability are summarized. Finally, critical research directions that should be prioritized to expedite the commercialization of M-N-C catalysts are outlined.

High-entropy nanoalloy is reported to be a highly efficient and stable bifunctional oxygen catalyst, which important for the sustainable application of rechargeable zinc-air batteries. However, phase separation is a common issue in the preparation of high-entropy nanoalloy. Herein, the high-entropy nanoalloy was successfully constructed using molten salt electroreduction method. The bifunctional oxygen overpotential (ΔE) of the catalyst is as low as 0.72V. The zinc-air battery assembled with this catalyst exhibits exceptional peak power density (216.7 mW cm^-2) and specific capacity (784.4 mAh g^-1), with a cycling stability exceeding 1200 hours, among the best values reported to date in the field.

A stacked graphene nanosheet film that easily interlayer slips achieves columnar superdense lithium deposition and demonstrates exceptional plating/stripping stability.

The metallic nickel nano-network on the MoO ₂ surface facilitates rapid electron transfer to each active site and simultaneously shortens hydrogen spillover pathway, which significantly enhances hydrogen evolution activity at high current densities.