This Critical Review provides an overview of the recent developments in the synthesis and characterization of bimetallic nanoparticles. Initially the review follows a materials science perspective on preparing bimetallic nanoparticles with designer morphologies, after which the emphasis shifts towards recent developments in using these bimetallic particles for catalysing either oxidation or reduction. In the final part of this review we present an overview of the utilization of bimetallic catalyst systems for the transformation of bio-renewable substrates and reactions related to the realization of a bio-refinery. Because of the sheer number of examples of transformations in this area, a few key examples, namely selective oxidation, hydrogenation/hydrogenolysis and reforming of biomass derived molecules, have been chosen for this review. Reports of bimetallic catalysts being used for the aforementioned transformations are critically analysed and the potential for exploiting such bimetallic catalysts have also been highlighted. A specific objective of this review article is to motivate researchers to synthesize some of the “designer” bimetallic catalysts with specific nanostructures, inspired from recent advances in the area of materials chemistry, and to utilize them for the transformation of biomass derived materials that are very complex and pose different challenges compared to those of simple organic molecules. We consider that supported bimetallic nanoparticles have an important role to play as catalysts in our quest for a more green and sustainable society.

Selective oxidation of primary carbon-hydrogen bonds with oxygen is of crucial importance for the sustainable exploitation of available feedstocks. To date, heterogeneous catalysts have either shown low activity and/or selectivity or have required activated oxygen donors. We report here that supported gold-palladium (Au-Pd) nanoparticles on carbon or TiO₂ are active for the oxidation of the primary carbon-hydrogen bonds in toluene and related molecules, giving high selectivities to benzyl benzoate under mild solvent-free conditions. Differences between the catalytic activity of the Au-Pd nanoparticles on carbon and TiO₂ supports are rationalized in terms of the particle/support wetting behavior and the availability of exposed corner/edge sites.

A radical route from methane to methanol: The conversion of methane into chemicals usually proceeds through high-temperature routes that first form more reactive carbon monoxide and hydrogen. Agarwal et al. report a low-temperature (50°C) route in aqueous hydrogen peroxide (H ₂ O ₂ ) for oxidizing methane to methanol in high yield (92%). They used colloidal gold-palladium nanoparticles as a catalyst. The primary oxidant was O ₂ ; isotopic labeling showed that H ₂ O ₂ activated methane to methyl radicals, which subsequently incorporated O ₂ . Science , this issue p. 223

The direct hydrogenation of CO2 into methanol is crucial for providing a means of CO2 fixation and a way to store cleanly produced hydrogen in a more energy-dense and transportable form. Here we have prepared two series of Pd/ZnO catalysts, both by immobilisation of PVA-protected Pd colloids and by Pd impregnation of PdCl2 to investigate structure activity relationships for direct CO2 hydrogenation. Very different performances were found for the different preparation methods, and the Pd loading and pre-reduction of the catalysts were shown to be important factors for optimising methanol yield. The crucial factor for high methanol yield is the formation of a Pd–Zn alloy, either during the reaction itself, or better by high temperature pre-reduction. The formation of the alloy greatly reduces CO production by the reverse water gas shift reaction. The catalysts prepared by sol-immobilisation were relatively stable to thermal treatment. In contrast, the impregnated catalysts were much less thermally stable, due to the presence of remnant chloride on the surface of the catalyst, which was absent for the case of sol immobilisation preparation. The results illustrate the importance of controlling the PdZn particle size and its surface structure for the catalysts to achieve high methanol selectivity (60%, the rest being CO) and conversion (11%) at 250°C and 20bar. Selectivity for sol-immobilised catalysts decreases from 60% at 3nm average diameter, to 20% at 7nm