The development of biodegradable packaging materials has become a widely addressed topic in recent years. Microparticles generated from Brassica oleracea var. capitata f. rubra (red cabbage, RC) and Beta vulgaris L. var. conditiva (beetroot, BR) which contained anthocyanins or betalains, were included in the formulation of edible films based on cassava starch (CS) giving origin to films CSRC, CSBR, or CSBC (mixture of both particles). The inclusion of the filler determined an increase in the stress at rupture from 0.8 MPa (CS) to 1.2 MPa (CSRC) or 1.0 MPa (CSBC), of the contact angle from 2.6° to 13.8° (CSBR) or 19.6° (CSBC). The use of these films for developing a smart label for hake packaging and the study of the TBV-N content, the microbiological characteristics of the muscle, and the color changes of the label with time, allowed us to conclude that the films CSRC and CSBC would be suitable for sensing the deterioration of packaged and chilled hake and that the color change of the label CSBC was completely consistent with fish muscle deterioration. As the microparticles can be obtained from by-products of the production and industrialization of plant tissues, the composite films and the smart labels developed can contribute not only to the development of safe food but also to the addition of value to those residues and to environmental protection.

Sustainable corn starch nanoparticles were prepared using media milling to stabilize omega-3-rich Pickering emulsions based on chia oil. The milling conditions were as follows: 24 h (milling time), 0.4–0.6 mm (bead diameter), 1600 rpm (impeller speed), 30% (volume occupied by the grinding media), 7% w/v (starch concentration), and 0, 0.07 and 1% w/v of sodium dodecyl sulfate (SDS). Nanosuspensions containing 7% w/v of starch and the three concentrations of SDS were filtered, centrifuged, homogenized, and spray-dried to obtain redispersible powders. The particle size ranges were 2288 ± 211, 385 ± 21, and 278 ± 11 nm with 0, 0.07 and 1% w/v of SDS, respectively. The most stable backscattering profiles obtained during a period of one week were observed with 0.07 and 1% w/v of SDS. Therefore, the surface dilatational rheology of these particles adsorbed at chia oil/water interfaces was studied. A rapid decrease in the interfacial tension within 1 h was obtained with 1% w/v of SDS (down to 3 mN/m). Moreover, the most stable particle size after redispersion was obtained with the highest concentration of SDS. Finally, Pickering emulsions were prepared, and significant coalescence was observed with 0 and 0.07% w/v of SDS (within a few minutes). Nonetheless, in the presence of 1% w/v of SDS, oil droplets showed mean diameters and polydispersity indexes of 280.13 ± 4.60 nm and 0.35 ± 0.02, respectively, with no significant variations during storage for around 1 month. The results show that wet-stirred media milling can be applied to produce sustainable, new food-grade starch nanoparticles able to deliver bioactive compounds from chia oil.