The chemical composition of wood is important to assess the quality of this raw material for the industry of cellulosic pulp production. The purpose of this work was to determine the chemical composition of Eucalyptus spp. grown for cellulosic pulp production. Ten Eucalyptus spp. clones with six years of age, located in the municipality of Itamarandiba, Minas Gerais, Brazil, were used. Quantification was obtained for extractives, monosaccharides, uronic acids, acetates, lignin, ash and the phenolic composition of the extracts. In average, clones showed around 2.7% extractives, with a predominance of polar compounds soluble in ethanol and water; 27.7% lignin and 0.3% ash. Glucose was the main sugar detected (64.2%), followed by xylose (19.3%). The main components of the extractives were steroids, fatty acids and aromatic acids, followed by smaller amounts of substituted alkanoic acids, fatty alcohols, glycerol derivatives and triterpenes. The ethanol–water extracts presented total phenol contents ranging from 321.4 to 586.6 mg EAG/g of extract, tannins from 28.1 to 65.1 mg catechin/g of extract and flavonoids from 73.6 to 256.9 mg catechin/g of extract. Clones with a higher holocellulose amount and a lower lignin content showed a higher potential for cellulosic pulp production. These findings are important for the development of high-quality wood based on important traits for the pulp and paper sector.

Charcoal production stands out as a raw material for the production of renewable energy. To assess wood quality in energy terms, studies have focused more on the holocellulose and lignin content than on the role of extractives. The objective of this study was to evaluate the relationship between the extractive content in cold water, in dichloromethane and total on energy properties of wood and charcoal, from six trees species. The extractives were removed with different solvents to be recorded and gross calorific value of wood was determined. The wood was carbonized at 1.67°C/min heating rate until maximum of 450°C and residence time of 30 min. The extractive content was correlated with the gravimetric yield, apparent relative density, ash, volatile matter, fixed carbon and gross calorific value of charcoal. The removal of total extractives and extractives soluble in dichloromethane reduced the gross calorific value of wood of most species evaluated. The extractives removed in cold water did not correlate with the parameters of carbonization. The extractives content in dichloromethane correlated with volatile matter, fixed carbon and gross calorific value. Total extractive content correlated with gravimetric yield, apparent relative density and gross calorific value of charcoal.

The energy potential of wood biomass is significantly shaped by its chemical composition. Analyzing the chemical composition of wood biomass and understanding the correlations between these parameters and wood combustibility are essential stages in the selection process of Eucalyptus clones tailored for firewood production and energy generation. In this study, we aimed to evaluate the impact of chemical composition on the direct combustibility of Eucalyptus clones. We examined the structural chemical composition and conducted proximate analysis, including fixed carbon, volatile material, and ash, to investigate the relationship between proximate composition and wood combustibility parameters. Our findings revealed significant correlations between wood chemical composition and combustibility parameters. In particular, lignin content, ethanol-soluble extractives, and xylose demonstrated inverse relationships with the parameters of maximum combustion rate, combustion characteristic index, and ignition index. Conversely, holocellulose content, cold-water-soluble extractives, and glucose exhibited direct correlations with the same combustibility parameters. Furthermore, fixed carbon and volatile matter contents demonstrated direct and inverse correlations, respectively, with ignition temperature. These findings have significant implications for enhancing the efficiency and sustainability of biomass energy production.

Drying is an important step to using wood and anatomical characteristics influence this process. Thus, the objective of this work was to evaluate the relationship between anatomy and wood drying. Samples with 2 x 2 x 4 cm were obtained from eight Eucalyptus urophylla x Eucalyptus grandis clones at 1.3 m height to evaluate the anatomy and drying in climate chamber during 15 days. Cell wall fraction was established as the parameter that best correlated with drying, the Pearson correlation coefficient between this parameter and moisture was -0.8986, -0.6580, 0.9216, 0.8743, 0.7131 and 0.8727 for saturated wood, and after 1, 2.5, 5, 10 and 15 days of drying, respectively. The frequency and vessel size, as well as the height and width of the rays showed low relation with wood drying. Wood anatomy, mainly the cell wall fraction, influences moisture losses and should be considered in wood drying programs.