Perovskite solar cells (PSCs) have rapidly become a hot area of research in the photovoltaic field due to their (e.g., 26.2%), ease of fabrication, and low cost. Over the last decade the electron transport layer (ETL) has been one of the most critical elements in achieving high-performing solar cells, necessitating a higher electron mobility and superior charge extraction ability. Consequently, there is a significant demand for an improved ETL that is not only cost-effective but also exhibits high charge extraction and mobility, particularly in the context of planar solar cell architecture. Tin Oxide (SnO₂) has emerged as one of the most promising high-performance inorganic ETLs suitable for PSCs. In this work, we synthesize solution-processed SnO₂. The spin-coated SnO₂ thin films undergo annealing at relatively low temperatures ranging from 130 °C to 180 °C and various characterization tools are employed for the evaluation of thin films.

The present work is on the synthesis and investigation of the structural, optical, and optoelectrical properties of NbSe₂ as an efficient material for energy conversion applications. The liquid phase exfoliation method was employed for the synthesis of 2D nanosheets from the bulk NbSe₂ at different exfoliation levels. SEM was used to confirm the physical dimensions of the nanosheets, while XRD was used to verify the structural retention of hexagonal nanosheets. The results demonstrate that high-quality, single-crystalline NbSe₂ nanosheets with a size of ≈1 μm in the lateral dimension and ≈6–12 nm thick were obtained. The 2D nanosheets will be further explored for energy storage and conversion applications.

All inorganic perovskite colloidal nano crystals are an emerging class of optoelectronic materials. However, their colloidal and structural stability during isolation and washing are major hurdles for their commercial application. Their intrinsic chemical instability and optical stability are directly related to the bonding nature of the nanocrystals’ surface and organic capping agents that passivate the surface of nanocrystals. We studied the surface ligand properties of CsPbBr3 prepared by the conventional hot injection method and their washing with varying polarity antisolvent. We observed changes in electrical and optical properties through experimental studies. The study was mainly done by optical and electronic measurements. We determined a facile nanocrystal washing protocol and observed a considerable improvement in the optoelectronic properties of the all-inorganic perovskite colloidal nanocrystals.