To explore the influence of different welding modes on the properties of 316L thin-plate welded joints, a new type of laser arc compound gun head similar to a coaxial one was used in this experiment. A high-speed camera was used to record the welding process and analyze the droplet splash behavior of the molten pool. The microstructure, microhardness change, and tensile test results of welded joints under different welding modes were analyzed. The results showed that laser welding (LW) is more prone to molten pool splash than hybrid laser arc welding (HLAW). The HLAW pool area was significantly increased compared with that of LW. The HLAW joint microstructure was more uniform than that of LW, which can improve the microhardness of welded joints. HLAW improved the tensile properties of the joint, with the maximum tensile strength of the joint increasing from 433 to 533 MPa. This test can provide guidance for the HLAW process.

The high cooling rate and temperature gradient caused by the rapid heating and cooling characteristics of laser welding (LW) leads to excessive thermal stress and even cracks in welded joints. In order to solve these problems, a dynamic preheating method that uses hybrid laser arc welding to add an auxiliary heat source (arc) to LW was proposed. The finite element model was deployed to investigate the effect of dynamic preheating on the thermal behavior of LW. The accuracy of the heat transfer model was verified experimentally. Hardness and tensile testing of the welded joint were conducted. The results show that using the appropriate current leads to a significantly reduced cooling rate and temperature gradient, which are conducive to improving the hardness and mechanical properties of welded joints. The yield strength of welded joints with a 20 A current for dynamic preheating is increased from 477.0 to 564.3 MPa compared with that of LW. Therefore, the use of dynamic preheating to reduce the temperature gradient is helpful in reducing thermal stress and improving the tensile properties of the joint. These results can provide new ideas for welding processes.