The role of the oral microbiome and its effect on dental diseases is gaining interest. Therefore, it has been sought to decrease the bacterial load to fight oral cavity diseases. In this study, composite materials based on chitosan, chitosan crosslinked with glutaraldehyde, chitosan with zinc oxide particles, and chitosan with copper nanoparticles were prepared in the form of thin films, to evaluate a new alternative with a more significant impact on the oral cavity bacteria. The chemical structures and physical properties of the films were characterized using by Fourier transform infrared spectroscopy (FTIR,) Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), elemental analysis (EDX), thermogravimetric analysis (TGA), X-ray diffraction (XRD), scanning electron microscopy (SEM), and contact angle measurements. Subsequently, the antimicrobial activity of each material was evaluated by agar diffusion tests. No differences were found in the hydrophilicity of the films with the incorporation of ZnO or copper particles. Antimicrobial activity was found against S. aureus in the chitosan film crosslinked with glutaraldehyde, but not in the other compositions. In contrast antimicrobial activity against S. typhimurium was found in all films. Based on the data of present investigation, chitosan composite films could be an option for the control of microorganisms with potential applications in various fields, such as medical and food industry.

Copper nanoparticles (NCu) were synthetized and added to commercial glass ionomer cement, to evaluate in vitro its antibacterial activity against oral cavity strains. The NCu were synthesized by copper acetate reduction with L-ascorbic acid and characterized by FTIR, Raman, XPS, XRD and TEM. Then, commercial glass ionomer cement (GIC) was modified (MGIC) with various concentrations of NCu and physicochemically characterized. Cell viability was tested against human dental pulp fibroblasts (HDPFs) by Alamar-Blue assay and antibacterial test was performed against S. mutans and S. sanguinis by colony forming unit (CFU) growth method. Synthesized NCu rendered a mixture of both metallic copper and cuprous oxide (Cu2O). HDPF viability reduces with exposure time to the extracts (68–72% viability) and MGIC with 2–4 wt% NCu showed antimicrobial activity against the two tested strains.