Biosynthesizing of silver nanoparticles using microorganisms or various plant parts have proven more environmental friendly, cost-effective, energy saving and reproducible when compared to chemical and physical methods. This investigation demonstrated the plant-mediated synthesis of silver nanoparticles using the aqueous leaf extract of Thevetia peruviana. UV–Visible spectrophotometer was used to measure the surface plasmon resonance of the nanoparticles at 460 nm. Fourier Transform Infrared showed that the glycosidic –OH and carbonyl functional group present in extract were responsible for the reduction and stabilization of the silver nanoparticles. X ray diffraction, Scanning Electron Microscopy, Transmission Electron Microscopy and Selected Area Electron Diffraction analyses were used to confirm the nature, morphology and shape of the nanoparticles. The silver nanoparticles are spherical in shape with average size of 18.1 nm. The synthesized silver nanoparticles showed activity against fungal pathogens and bacteria. The zone of inhibition observed in the antimicrobial study ranged between 10 and 20 mm.

Biosynthesized silver nanoparticles (AgNPs) usingCassia hirsutaaqueous leaf extract were reported in this study. The synthesis was optimized by measuring various parameters such as temperature, time, volume ratio, and concentration. The surface plasmon resonance at 440 nm for 30°C and 420 nm for both 50°C and 70°C measured using the UV-Vis spectrophotometer confirmed the formation of AgNPs synthesized usingC.hirsuta(CAgNPs). The functional groups responsible for the reduction and stabilization of the NPs were identified using Fourier Transform Infrared (FTIR). The morphology, size, and elemental composition of the NPs were obtained using scanning electron microscope (SEM), transmission electron microscope (TEM), and energy dispersive X-ray spectroscopy (EDX). X-ray diffractometer was used to identify the phases and crystallinity of CAgNPs. Crystalline spherical NPs with average diameter of 6.9 ± 0.1 nm were successfully synthesized. The thermal analysis of CAgNPs was observed from DSC-TGA. The larvicidal results against the different larva instar stage ofCulex quinquefasciatusgave LC₅₀= 4.43 ppm and LC₉₀= 8.37 ppm. This is the first study on the synthesis of AgNPs usingC.hirsutaand its application against lymphatic filariasis vector. Hence, it is suggested that theC.hirsutasynthesized AgNPs would be environmentally benign in biological control of mosquito.