The paper reports on the properties of UV-curable inorganic-organic hybrid polymer multimode optical channel waveguides fabricated by roll-to-plate (R2P) nanoimprinting. We measured transmission spectra, refractive indices of the applied polymer materials, and optimized the R2P fabrication process. Optical losses of the waveguides were measured by the cut-back method at wavelengths of 532, 650, 850, 1310, and 1550 nm. The lowest optical losses were measured at 850 nm and the lowest average value was 0.19 dB/cm, and optical losses at 1310 nm were 0.42 dB/cm and 0.25 dB/cm at 650 nm respectively. The study has demonstrated that nanoimprinting has great potential for the implementation of optical polymer waveguides not only for optical interconnection applications.

Silk fibroin protein has been reinvented as a new optical material for biophotonic applications because of its optical transparency, biocompatibility, and easy fabrication process. It is used in various silk-based optical devices, which makes it desirable to investigate the optical properties of silk from diverse perspectives. This paper presents our investigation of the optical properties of silk fibroin, extracted from Bombyx mori cocoons. We have measured transmission spectra from the visible to near-infrared region and investigated waveguiding properties by the prism-coupling technique for five wavelengths (473.0, 632.8, 964.0, 1311, and 1552 nm). From the measurements, we determined the values of refractive indices. The measurements also proved waveguiding properties for all of the wavelengths. Optical scattering losses were measured by the fiber probe technique at 632.8 nm and were estimated to be 0.22 dB·cm⁻¹.

The influence of the addition of Y₂O₃ on the structural, spectroscopic, and laser properties of newly prepared Er, Yb-doped strontium-sodium phosphate glass was investigated. While the addition of Y₂O₃ has a small influence on the absorption spectra and fluorescence lifetime, it has a strong impact on the emission cross-section and on OH⁻ content. The glasses were used as the active medium for diode-pumped laser emitting at 1556 nm. The increase in Y₂O₃ content leads to a significant 35% increase in laser slope efficiency up to 10.4%, but at the expense of the substantial reduction of the wavelength tunability from 82 to 54 nm.