Chitosan is a biopolymer with unique properties that have attracted considerable attention in various scientific fields in recent decades. Although chitosan is known for its poor electrical and mechanical properties, there is interest in producing chitosan-based materials reinforced with carbon-based materials to impart exceptional properties such as high electrical conductivity and high Young’s modulus. This study describes the synergistic effect of carbon-based materials, such as reduced graphene oxide and carbon nanotubes, in improving the electrical, optical, and mechanical properties of chitosan-based films. Our findings demonstrate that the incorporation of reduced graphene oxide influences the crystallinity of chitosan, which considerably impacts the mechanical properties of the films. However, the incorporation of a reduced graphene oxide–carbon nanotube complex not only significantly improves the mechanical properties but also significantly improves the optical and electrical properties, as was demonstrated from the photoluminescence studies and resistivity measurements employing the four-probe technique. This is a promising prospect for the synthesis of new materials, such as biopolymer films, with potential applications in optical, electrical, and biomedical bioengineering applications.

The major issue associated with thermoelectric performance is the low efficiency of power conversion. The main challenge is achieving a combination of high Seebeck coefficient, high electrical conductivity, and low thermal conductivity for a significantly improved figure of merit (ZT). Developing strategies include the production of tetrahedrites with an intrinsically low thermal conductivity through the solvothermal method, using a low reaction time and processing temperature. Here, we report on the preparation of Cu-rich tetrahedrites through the solvothermal technique at low temperature, providing a promising strategy for the preparation of materials with potential applications in thermoelectricity. The influence of synthesis reaction time and temperature on the morphological, structural, and thermoelectrical properties of the samples was investigated through different characterization techniques. Tetrahedrite synthesized at 180 °C for 19 h yielded a favorable ZT value of >0.43 and a thermal conductivity of 0.2 Wm⁻¹ K⁻¹ (423 K), related to the Sb³⁺/Sb⁵⁺ and Cu⁺/Cu²⁺ ratio, as was observed by XPS. The cubic tetrahedrite phase attributed to the (222) plane was confirmed by XRD and TEM and the intense Raman mode observed at 351 cm⁻¹. SEM images revealed that nanotetrahedral Cu-rich tetrahedrites efficiently assemble into spherical structures, resulting in an improvement in the Seebeck coefficient (437 µVK⁻¹) and electrical conductivity.