Laser structuring can be applied to composite electrodes of lithium-ion cells to enhance wetting and to facilitate the usage of thick-film electrodes by reducing the lithium-ion diffusion overpotential and the tortuosity of the electrodes or the usage of electrodes containing silicon, where additional porosity is required to compensate the volume expansion during lithium de-/insertion. To integrate the additional laser processing step in the well-established electrode manufacturing route, the laser processing speed must be significantly increased to match with the belt speed, which is dependent on the electrode thickness and the type of manufacturing route. Upscaling can be realized by increasing the average laser power, laser intensity, and/or laser repetition rate. Here, an ultrashort pulsed laser source with an average power of 300 W and a pulse duration of 600 fs was applied. For the first time, the presented research provides detailed laser ablation processing data for thick-film composite anodes associated with high repetition rates ranging from 4.9 to 48.8 MHz. The patterning results are compared depending on the widths, depths, aspect ratios, the total appearance regarding debris and cracks, and the volume ablation rate. In high repetition rate laser patterning, the subsequent laser pulses interact with the material vapor plasma generated by the previous laser pulses, resulting in lower ablation depths and higher ablation widths. The increase in laser peak intensity leads to higher achievable ablation depths. Processing strategies are identified for two different ablation scenarios focusing on the pouch cells of a Volkswagen ID.3 and the Tesla 4680 cell.

The most common pattern types for anode structuring, in particular the line, grid, and hexagonal-arranged hole pattern were evaluated in a comparable setup in full-cells and symmetrical cells. The cells with structured electrodes were compared to reference cells with unstructured anodes of similar areal capacity (4.3 mAh cm⁻²) and the onset of lithium plating during fast-charging was determined in situ by differential voltage analysis of the voltage relaxation and ex situ by post-mortem analysis. Furthermore, electrochemical impedance spectroscopy measurements on symmetrical cells were used to determine the ionic resistance of structured and unstructured electrodes of similar areal capacity. All cells with structured electrodes showed lower ionic resistances and an onset of lithium plating shifted to higher C-rates compared to cells with unstructured electrodes. The structure patterns with capillary structures, i.e., lines and grids, showed significant reduced lithium plating during fast-charging and a higher rate capability compared to reference cells with unstructured electrodes and cells with hole structured electrodes. The continuous rewetting of the electrode with liquid electrolyte by capillary forces and the reduced ionic resistance of the 3D electrode are identified as key factors in improving overall battery performance. The data of the studied cells were used to calculate the resulting energy and power densities of prospective commercial pouch cells and potential pitfalls in the comparison to cells with unstructured electrodes were identified.

Lithium-ion batteries are currently one of the most important energy storage devices for various applications. However, it remains a great challenge to achieve both high energy density and high-power density while reducing the production costs. Cells with three-dimensional electrodes realized by laser ablation are proven to have enhanced electrochemical performance compared to those with conventional two-dimensional electrodes, especially at fast charging/discharging. Nevertheless, laser structuring of electrodes is still limited in terms of achievable processing speed, and the upscaling of the laser structuring process is of great importance to gain a high technology readiness level. In the presented research, the impact of different laser structuring strategies on the electro-chemical performance was investigated on aqueous processed Li(Ni₀.₆Mn₀.₂Co₀.₂)O₂ cathodes with acid addition during the slurry mixing process. Rate capability analyses of cells with laser structured aqueous processed electrodes exhibited enhanced performance with capacity increases of up to 60 mAh/g at high current density, while a 65% decrease in ionic resistance was observed for cells with laser structured electrodes. In addition, pouch cells with laser structured acid-added electrodes maintained 29–38% higher cell capacity after 500 cycles and their end-of-life was extended by a factor of about 4 in contrast to the reference cells with two-dimensional electrodes containing common organic solvent processed polyvinylidene fluoride binder.