Automotive catalysts containing Platinum Group Metals (PGMs) are valuable secondary raw materials for refineries. Hydrometallurgical processing of catalysts is ineffective due to the low PGMs content—0.15–0.3%. Therefore, such raw materials are melted into an iron collector containing 1.5–5% PGMs. However, when leaching a collector containing 10–20% Si in both HCl and H₂SO₄, the recovery of PGMs does not exceed 40%. The latter indicates incomplete destroying of the PGM-encapsulating ferrosilicon matrix. To completely destroy the ferrosilicon matrix, it is proposed to carry out the leaching process in a mixture of HCl and HF. In this case, the extraction of Fe into solution and Si into the gas phase (in the form of SiF₄) exceeds 90%. This should be sufficient to completely destroy the ferrosilicon matrix and release PGMs. The current work presents the results of studies of the leaching kinetics of the iron collector containing ferrosilicon in a mixture of HCl and HF using the Shrinking Core Model (SCM). It was found that the greatest positive effect on Fe extraction into solution is exerted by HCl concentration and temperature, while Si release into the gas phase is only influenced by HF concentration. In addition, during the destroying of ferrosilicon, FeF₂ is formed and deposited on the surface of the material in the form of thin-film conglomerates. This leads to diffusion difficulties and a gradual decrease in the intensity of the iron collector leaching 30 min after the start of process. After 120 min, there may be a decrease in Fe recovery into solution.

The leaching kinetics of an industrial iron collector containing PGMs (Pd, Pt, Rh) in HCl and HF solutions were investigated. The effects of the HCl concentration (2.74–6.86 mol/L), the HF concentration (1.46–7.50 mol/L), temperature (323–363 K), and leaching time (0–210 min) on the extraction of Fe into the solution and Si into the gas phase from the iron collector were studied. The HCl concentration had a negative effect on the extraction of Si, which decreased from 78.2% to 58.1% and from 97.4% to 87.2% in the time ranges of 0–30 min and 30–120 min, respectively. This occurred due to the accumulation of Fe²⁺ in the solution and its interaction with HF, which led to a reduction in both the HF concentration and the extraction of Si. In addition, there were diffusion difficulties of the Fe and Si extraction because Fe precipitated on the surface of the cakes in the form of thin-film conglomerates of FeF₂. This was confirmed by the XRF and EDS results, indicating that F was present on the surface of the cakes. The processes of the Fe and Si extraction were diffusion-chemically controlled and diffusion controlled—the apparent activation energies decreased from 26.9 kJ/mol to 7.8 kJ/mol and from 2.2 kJ/mol to 2.0 kJ/mol in the time range of 0–120 min, respectively. Using the shrinking core model and the full factorial experiment model, the kinetic equations, the optimal parameters of iron collector leaching, and the extraction rates of Fe and Si were determined. These optimal parameters ensure the extraction of Fe and Si at the level of 95% with high leaching rates: the HCl concentration of 4.36 mol/L, the HF concentration of 6.93 mol/L, temperature of 363 K, and leaching time of 80 min.