Although ultra high-performance concrete (UHPC) has great performance in strength and durability, it has a disadvantage in the environmental aspect; it contains a large amount of cement that is responsible for a high amount of CO₂ emissions from UHPC. Supplementary cementitious materials (SCMs), industrial by-products or naturally occurring materials can help relieve the environmental burden by reducing the amount of cement in UHPC. This paper reviews the effect of SCMs on the properties of UHPC in the aspects of material properties and environmental impacts. It was found that various kinds of SCMs have been used in UHPC in the literature and they can be classified as slag, fly ash, limestone powder, metakaolin, and others. The effects of each SCM are discussed mainly on the early age compressive strength, the late age compressive strength, the workability, and the shrinkage of UHPC. It can be concluded that various forms of SCMs were successfully applied to UHPC possessing the material requirement of UHPC such as compressive strength. Finally, the analysis on the environmental impact of the UHPC mix designs with the SCMs is provided using embodied CO₂ generated during the material production.

A calcium carbonate (CaCO₃)-based coating with gamma-C₂S (γ-C₂S) as the main carbonatable binder is proposed to protect the metal substrate against corrosion in this paper. Here, the morphology and phase assemblage of the coatings are studied by scanning electron microscopy (SEM) and X-ray diffraction (XRD), and the corrosion resistance of the coating is evaluated by electrochemical impedance spectroscopy (EIS) and X-ray photoelectron spectroscopy (XPS). Results show that the carbonated coating has excellent properties in terms of ultraviolet (UV) aging resistance, salt fog resistance, and electrochemical corrosion resistance. The porosity of deposited coating on steel substrates decreases by 47.1% after carbonation due to the compacted calcium carbonate formation, which is recognized as a self-compacting process during carbonation. The coating also exhibits rapid strength development within the first 2 h of carbonation; both the CO₂ uptake efficiency and degree of carbonation (DOC) can reach more than 95% of the total CO₂ uptake efficiency and final DOC values. This study provides a novel insight to extend the category of inorganic coating with additional benefits of CO₂ solidification.