A series of new environment-friendly plasticizers was synthesized from castor oil and used to plasticize nitrile rubber (NBR). The test results showed that tensile strength, elongation at break, and tear strength of NBR vulcanizates plasticized by castor oil-based plasticizers were found to be better than that of dioctyl phthalate (DOP). The aging test taken demonstrated that the castor oil-based plasticizers could improve the hot air and oil aging resistance of NBR vulcanizates. The thermal stability test illustrated that castor oil-based plasticizers enhanced the thermal stability of NBR vulcanizates, and the initial decomposition temperatures (T_10%) were about 100 °C higher than that of DOP. In general, the studies manifested that EACO and EBCO can replace DOP to plasticize NBR and are used in fields that require high mechanical properties, aging resistance, and thermal stability. This study emphasizes the effects of sustainable, cost-effective, and high-efficiency plasticizers on NBR.

Developing a highly efficient multifunctional epoxy adhesive is still an enormous challenge, which can rapidly cure at room temperature and has excellent low-temperature resistance performance and is crucial for the epoxy adhesive and electrical sealing fields during severe cold seasons. Herein, diglycidyl phthalate (DP) was synthesized with phthalic anhydride (PA) and epichlorohydrin (ECH) to enhance the curing rate and low-temperature resistance of bisphenol A diglycidyl ether (DGEBA) adhesive. The modified DP/DGEBA adhesives were systematically analyzed by gel time, mechanical properties, and aging resistance (time, temperature, and dry/wet treatment). The results showed that DP with highly active ester groups significantly accelerates the curing speed of DP/DGEBA. DP's rigid aromatic ring-benzene ring and flexible group-ester group gave the adhesive better low-temperature resistance. When the addition of DP was 10 wt % (based on the mass of DGEBA), the gel time of DP/DGEBA epoxy adhesives was reduced by 58 min compared to unmodified DGEBA epoxy adhesive, and after aging at low temperature (-20 °C) for 7 days, the tensile shear strengths of polyvinyl chloride (PVC) and aluminum plate increased by 76.2 and 80.6%, respectively. The results of non-isothermal curing kinetics and dynamic mechanical analysis suggested that when the amount of DP was 10 wt %, the reaction activation energy of DP/DGEBA epoxy adhesive decreased by 4.0%, and the cross-linking density increased by 8.9%. Moreover, the toughness of the modified adhesive was also improved. This study opens up a feasible way for the development of a low temperature-resistant epoxy adhesive cured rapidly at room temperature in practical application.

Rapidly developing technology places higher demands on materials, thus the simultaneous improvement of materials’ multiple properties is a hot research topic. In this work, a high-branched silicone epoxy resin (QSiE) was synthesized and applied to the curing system of bisphenol A epoxy resin (DGEBA) for modification investigations. When 6 wt% QSiE was added to the system, the viscosity dropped by 51.8%. The mechanical property testing results indicated that QSiE could significantly enhance the material’s toughness while preserving good rigidity. The impact strength was enhanced by 1.31 times when 6wt% of QSiE was introduced. Additionally, the silicon skeleton in QSiE has low surface energy and low polarizability, which could endow the material with good hydrophobic and dielectric properties. This work provided a new idea for the preparation of high-performance epoxy resin additives, and provided a broad prospect for cutting-edge applications of epoxy resins.