Situated in the village of Lama Temple on the eastern bank of the Wulie River in Chengde, Puren Temple stands as one of the few remaining royal temples of great importance from the Kangxi era (1662–1722 AD). This ancient edifice has greatly contributed to the advancement of our comprehension regarding the art of royal temple painting. The present study undertakes a comprehensive analysis and identification of nine samples obtained from the beams and ceiling paintings within the main hall of Puren Temple. Furthermore, a systematic examination of their mineral pigments and adhesives is conducted. The findings from polarized light microscopy (PLM), energy-type X-ray fluorescence spectrometer (ED-XRF), micro-Raman spectroscopy (m-RS), and X-ray diffractometer (XRD) analyses reveal that the pigments present in the main hall beams of Puren Temple are cinnabar, lead white, lapis lazuli, and lime green, while the pigments in the ceiling paintings consist of cinnabar, staghorn, lead white, lapis lazuli, and lime green. The use of animal glue as a binder for these pigments on both the main hall beams and ceiling paintings is confirmed via pyrolysis-gas chromatography–mass spectrometry (Py-Gc/Ms) results. These findings hold significant implications for the future restoration of Puren Temple, as they provide valuable guidance for the selection of appropriate restoration materials.

Cangjie Temple was built to commemorate Cangjie, the legendary inventor of Chinese characters. It stands as one of the few remaining temples in China dedicated to the invention and creation of writing. In this study, the material properties of wooden paintings from the Cangjie temple were characterized using Polarized Light Microscopy (PLM), Scanning Electron Microscopy coupled with Energy Dispersive X-ray Spectroscopy (SEM-EDS), Micro-confocal Raman Spectroscopy, X-ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), and Pyrolysis-Gas Chromatography-Mass Spectrometry (Py-GC/MS). It was confirmed that the pigments of the paintings included cinnabar, lapis lazuli, lead white, Paris green, and carbon black. The proteinaceous glue was used as an adhesive in the pigment samples, with tung oil likely being utilized as a primer for the wooden structures before painting. This study not only provides valuable data support for the conservation and restoration of the architectural features of Cangjie Temple but also provides useful reference for the maintenance and inheritance of similar ancient buildings.

The durability of wooden heritage objects and sites can be affected by external environmental factors, leading to decay, cracking, and other forms of deterioration, which might ultimately result in significant and irreversible loss. In this study, a FEVE resin was modified with Ag₂O/OH-MWCNTS (MA), denoted as MAF, where three concentrations were prepared using in situ precipitation, and the resulting composite adhesive was characterized by a high viscosity and effective bacteriostatic properties, demonstrating a better viscosity and thermal stability, as well as antibacterial properties, than pure FEVE resin. The results show that MAF adhesives present good thermal stability, as evidenced by a lower mass loss rate following treatment at 800 °C compared to the pure FEVE resin. At a consistent shear rate, the viscosity of MAF demonstrates a notable increase with the proportion of MA, which is better than that of FEVE. This suggests that the nano-Ag₂O particles in MA act as physical crosslinking agents in FEVE, improving the viscosity of the composite adhesive MAF. The adhesion strength between MAF and wood exhibits a similar trend, with wooden samples showing higher shear strengths as the proportion of MA increases in comparison to FEVE. Simultaneously, the antibacterial effects of the MAF adhesive exceeded 1 mm for Trichoderma, Aspergillus niger, and white rot fungi. The antibacterial activity of the MAF adhesive exhibited a direct correlation with the concentration of Ag₂O/OH-MWCNTS, with the most pronounced inhibitory effect observed on Trichoderma. The MAF adhesive demonstrates promising prospects as an adhesive for wooden heritage artifacts, offering a novel approach for the rapid, environmentally friendly, and efficient development of composite adhesives with superior adhesive properties.