In this work, the AISI 9840 steel was subjected to the powder-pack boriding in the temperature range of 1123–1273 K for various times ranging from 2 to 8 h. A kinetic model based on the principle of mass conservation at the growing interface was used to estimate the boron diffusion coefficients through the Fe₂B layers. The pack-borided samples were experimentally characterized by different techniques such as: Scaning electron microscopy, XRD analysis, Microhardness Vickers testing. The Daimler-Benz Rockwell-C indentation technique was used to assess the adhesion quality of boride coatings on AISI 9840 steel. Finally, the scratch and pin-on-disc tests for wear resistance were respectively performed using an LG Motion Ltd and a CSM tribometer under dry sliding conditions. The boron activation energy for the AISI 9840 steel was estimated as 193.08 kJ /mol by applying the present model. To confirm and extend the validity of the diffusion model, the experimental values of Fe₂B layers thicknesses obtained for other boriding conditions were compared with the predicted values.

In this present study, the AISI 1025 steel was pack-borided in the temperature range of 1,123–1,273 K for different treatment times ranging from 2 to 8 h. A diffusion model was suggested to estimate the boron diffusion coefficients in the Fe₂B layers. As a result, the boron activation energy for the AISI 1025 steel was estimated as 174.36 kJ/mol. This value of energy was compared with the literature data. To extend the validity of the present model, other additional boriding conditions were considered. The boride layers formed on the AISI 1025 steel were characterized by the following experimental techniques: scanning electron microscopy, X-ray diffraction analysis and the Daimler–Benz Rockwell-C indentation technique. Finally, the scratch and pin-on-disc tests for wear resistance were achieved using an LG Motion Ltd and a CSM tribometer, respectively, under dry sliding conditions.