Glass is increasingly desired as a material for manufacturing complex microscopic geometries, from the micro-optics in compact consumer products to microfluidic systems for chemical synthesis and biological analyses. As the size, geometric, surface roughness, and mechanical strength requirements of glass evolve, conventional processing methods are challenged. We introduce microscale computed axial lithography (micro-CAL) of fused silica components, by tomographically illuminating a photopolymer-silica nanocomposite that is then sintered. We fabricated three-dimensional microfluidics with internal diameters of 150 micrometers, free-form micro-optical elements with a surface roughness of 6 nanometers, and complex high-strength trusses and lattice structures with minimum feature sizes of 50 micrometers. As a high-speed, layer-free digital light manufacturing process, micro-CAL can process nanocomposites with high solids content and high geometric freedom, enabling new device structures and applications.

Volumetric additive manufacturing (VAM) forms complete 3D objects in a single photocuring operation without layering defects, enabling 3D printed polymer parts with mechanical properties similar to their bulk material counterparts. This study presents the first report of VAM‐printed thiol‐ene resins. With well‐ordered molecular networks, thiol‐ene chemistry accesses polymer materials with a wide range of mechanical properties, moving VAM beyond the limitations of commonly used acrylate formulations. Since free‐radical thiol‐ene polymerization is not inhibited by oxygen, the nonlinear threshold response required in VAM is introduced by incorporating 2,2,6,6‐tetramethyl‐1‐piperidinyloxy (TEMPO) as a radical scavenger. Tuning of the reaction kinetics is accomplished by balancing inhibitor and initiator content. Coupling this with quantitative measurements of the absorbed volumetric optical dose allows control of polymer conversion and gelation during printing. Importantly, this work thereby establishes the first comprehensive framework for spatial–temporal control over volumetric energy distribution, demonstrating structures 3D printed in thiol‐ene resin by means of tomographic volumetric VAM. Mechanical characterization of this thiol‐ene system, with varied ratios of isocyanurate and triethylene glycol monomers, reveals highly tunable mechanical response far more versatile than identical acrylate‐based resins. This broadens the range of materials and properties available for VAM, taking another step toward high‐performance printed polymers.

Volumetric additive manufacturing (VAM) enables rapid printing into a wide range of materials, offering significant advantages over other printing technologies, with a lack of inherent layering of particular note. However, VAM suffers from striations, similar in appearance to layers, and similarly limiting applications due to mechanical and refractive index inhomogeneity, surface roughness, etc. We hypothesize that these striations are caused by a self-written waveguide effect, driven by the gelation material nonlinearity upon which VAM relies, and that they are not a direct recording of non-uniform patterning beams. We demonstrate a simple and effective method of mitigating striations via a uniform optical exposure added to the end of any VAM printing process. We show this step to additionally shorten the period from initial gelation to print completion, mitigating the problem of partially gelled parts sinking before print completion, and expanding the range of resins printable in any VAM printer.

Cholesteric liquid crystal elastomers (CLCEs) hold great promise for mechanochromic applications in anti‐counterfeiting, smart textiles, and soft robotics, thanks to the structural color and elasticity. While CLCEs are printed via direct ink writing (DIW) to fabricate free‐standing films, complex 3D structures are not fabricated due to the opposing rheological properties necessary for cholesteric alignment and multilayer stacking. Here, 3D CLCE structures are realized by utilizing coaxial DIW to print a CLC ink within a silicone ink. By tailoring the ink compositions, and thus, the rheological properties, the cholesteric phase rapidly forms without an annealing step, while the silicone shell provides encapsulation and support to the CLCE core, allowing for layer‐by‐layer printing of self‐supported 3D structures. As a demonstration, free‐standing bistable thin‐shell domes are printed. Color changes due to compressive and tensile stresses can be witnessed from the top and bottom of the inverted domes, respectively. When the domes are arranged in an array and inverted, they can snap back to their base state by uniaxial stretching, thereby functioning as mechanical sensors with memory. The additive manufacturing platform enables the rapid fabrication of 3D mechanochromic sensors thereby expanding the realm of potential applications for CLCEs.

Shape memory polymers (SMPs) capable of recovering from a deformed state through heating were 3D printed using volumetric additive manufacturing, which enabled the layerless, single-step fabrication of self-standing tripod and actuating gripper structures.