Wooden shipwrecks are a significant part of the underwater cultural heritage. In 2007, the Nanhai No. 1 shipwreck was salvaged from the seabed and moved into the Marine Silk Road Museum, where it is still stored in a water tank. We analysed the microbial communities colonizing the hull surface of the Nanhai No. 1 shipwreck during storage. Six samples exposed to air were collected from different spots of the ship that exhibited obvious microbial plaques. High-throughput sequencing revealed the bacterial community includes both aquatic and terrestrial species, while in the fungal community, Fusarium was the most abundant genus across all samples and accounted for 84.91% to 98.40% of the total community composition. Two Fusarium species were isolated from the samples and were identified as F. solani and F. oxysporum. Both of the isolates were able to degrade cellulose, but only F. solani had the ability to degrade lignin. Antimicrobial efficacy in inhibiting the growth of Fusarium was assessed with five kinds of biocides, and isothiazolinones exhibited specific inhibition of Fusarium growth. These results provide critical background information to protect and reduce the biodegradation and destruction of this important historical shipwreck, and inform efforts to protect other similar artifacts.

Archaeological wood is a kind of ‘new material’ that has deteriorated due to long-term degradation. The existing wood science theory and evaluation methods are not fully applicable to archaeological wood. Moreover, current physical-mechanical evaluation methods are inadequate for fragile archaeological wood due to their insufficient accuracy and the large sample amount required, causing difficulties in many necessary physical-mechanical repeatability tests. In light of these limitations, the representative samples on Nanhai No. 1, a merchant shipwreck in the Song Dynasty, were selected as the research objects in this paper. The shipwreck is a typical waterlogged wooden artifact. A quasi-nondestructive physical-mechanical evaluation technique for archaeological wood was developed with the thermomechanical analyzer (TMA). This study used TMA to evaluate the bending strength of representative waterlogged archaeological samples of Nanhai No. 1 shipwreck and sound wood with the same species. Besides, the thermal linear expansion coefficients in the ambient temperature range were obtained. The sizes of the samples used in the tests were only 2 mm × 8 mm × 0.3 mm and 1 cm × 1 cm × 1 cm, respectively. Bending strength results of archaeological wood by the TMA method conformed to the tendency that the bending strength decreases with the increase of decay degree. In addition, the longitudinal linear expansion coefficients of archaeological wood reached 80%–115% of those in the transverse grain direction, which were about 10 times higher than those of the sound wood. The linear expansion coefficients of archaeological wood in three directions were similar. Based on the results of Fourier transform infrared analysis (FT-IR), the significant differences in the physical-mechanical properties of the archaeological wood and the sound wood were induced to be mainly ascribed to the decomposition and the loss of hemicellulose in the archaeological wood. The cell wall substrate could not stabilize the cellulose skeleton, which led to the instability of the tracheid structure of the archaeological wood. This study provided a proven quasi-nondestructive method for the preservation state evaluation of waterlogged archaeological wood (WAW) from the Nanhai I shipwreck and other similar waterlogged wooden relics.

The goal of this research was to analyze the fungal community responsible for the biodeterioration of a pirogue in the National Maritime Museum of China and to make recommendations for the protection of this artifact. Molecular identification of fungal strains isolated from the surface of the pirogue and the air of the storage room that were most closely related to Cladosporium, Penicillium, Talaromyces and Trichoderma spp. DNA extracted from the samples was sequenced on the Illumina MiSeq platform. The results showed that the predominant fungal genera present were Penicillium sp., Cladosporium sp. and Exophiala sp. Thereafter, cellulose degradation experiments were carried out on the predominant fungi screened by pure culturing. Finally, we tested the sensitivity of the predominant fungal isolates to four biocides. This work suggests that we should pay more attention to Penicillium sp. and Cladosporium sp. in the protection of wooden artifacts, and environmental control is recommended as the main means of protecting the pirogue.

Nanhai No. 1, a shipwreck in the Southern Song Dynasty, China, has a history of more than 800 years. It was salvaged in 2007 and is now on display in the Guangdong Maritime Silk Road Museum. Due to the fact that the hull is a wooden cultural relic and exposed to the air, the biological corrosion and biodegradation caused by microorganisms are key problems of hull protection. At present, the antimicrobial agent Euxyl^® K100 (isothiazolinone) has a significant antimicrobial effect in the field, but it has a certain negative impact on the environment and archeologists. In order to reduce the use of chemical antimicrobial agents, we evaluated the inhibitory effects of cinnamaldehyde on the main destructive microorganisms of Nanhai No. 1. Cinnamaldehyde is the main active component of cinnamon, and has broad-spectrum antimicrobial properties. The paper diffusion method, gas diffusion method and minimum inhibitory concentration experiment were used to detect the inhibitory effects of cinnamaldehyde on the main microorganisms of Nanhai No. 1. We found that cinnamaldehyde had significant inhibitory effects on Bacillus tequilensis NK-NH5, Bacillus megaterium NK-NH10, Bacillus velezensis NK-NH11, Bacillus sp. NK-NH15, Bacillus sp. NK-NH16, Bacillus sp. NK-NH17, Fusariumsolani NK-NH1 and Scedosporiumapiospermum NK.W1-3. At the same time, cinnamaldehyde had more inhibitory effects on fungi than bacteria. Finally, we verified that cinnamaldehyde can effectively inhibit the growth of microorganisms in water, for storing the scattered wood blocks of the Nanhai No. 1 hull through laboratory simulation experiments. Cinnamaldehyde, as an environment-friendly antimicrobial agent, is of great significance to protecting water-saturated wooden relics from microbial corrosion and degradation in the future.

The Nanhai No. 1 was a wooden merchant ship of the Southern Song Dynasty, which wrecked and sank in the South China Sea, Yangjiang City, Guangdong Province, China. The Nanhai No. 1 shipwreck was salvaged as a whole in 2007 and began to be excavated in 2013. During the archaeology excavation, some of the hull wood fell off the hull. These waterlogged archaeological woods (WAW) were immersed in the buffer containing EDTA-2Na and isothiazolinone K100 for moisture stabilization, preliminary desalination, and microbial inhibition. We evaluated the properties of these WAW through testing the chemical components (including lignin, holocellulose, and ash content) of the wood, and monitoring the iron element content, anion and cation content in the buffer. At the same time, the microbial composition in the desalination buffer was also detected. The results showed that the holocellulose content in these WAW were much lower than in fresh wood. The ash content in these WAW decreased after desalination treatment. The iron element content, anion and cation content in the buffer were high and kept at a certain level after desalination treatment. At the same time, the problem of biodegradation in the buffer should be paid attention to. The comprehensive protection of WAW requires to combine wood properties and microbial problems. This study provides a reference for the protection of WAW from the Nanhai No. 1 shipwreck and other similar historical wood.

Organosilicon materials have shown potential as dehydration agents for waterlogged wooden artifacts. These materials can polymerize under normal conditions to form polymers with favorable mechanical strength, antibacterial properties, and aging resistance. However, the insolubility of most organosilicon hindered their penetration into waterlogged wood, which may lead to an unwanted cracking. This study aimed to evaluate the effectiveness of polydimethylsiloxane (PDMS) and hydroxy-terminated polydimethylsiloxane (PDMS-OH) with low viscosity and moderate reactivity for dehydrating waterlogged wooden artifacts from the Nanhai No.1 shipwreck. Four surfactants ((3–aminopropyl) triethoxysilane (APTES), alkyl polyoxyethylene ether (APEO), tri-methylstearylammonium chloride (STAC), and fatty alcohol polyoxyethylene ether (AEO)) and cosurfactant were employed to transform the two kinds of water-repellent silicone oils into eight groups of highly permeable oil-in-water (O/W) emulsions. Under the catalysis of a neutral catalyst, in situ polymerization occurred within the wood cells. Group P2-2 formulated with PDMS-OH and APEO showed the best efficiency in maintaining the dimensions of the wood during dehydration. The dehydrated wood exhibited a natural color and texture with a minimal volume shrinkage rate of 1.89%. The resulting polymer adhered uniformly to the cell walls, effectively reinforcing the wood cell structure. The weight percent gain of the wood was only 218%, and the pores of the cell lumen were well maintained for future retreatment. This method effectively controlled the sol–gel reaction process of the organosilicon and prevented damage to the wooden artifact during the dehydration process. Moreover, the dehydrated wood samples only experienced a low weight gain of 17% at 95% relative humidity (RH), indicating their great environmental stability.