Titanium alloy is widely used as oil drill pipe material because of its light weight, high strength, good toughness, corrosion resistance, fatigue resistance, and good process performance. However, due to its low hardness, poor wear resistance, serious oxidation at high temperature (700 °C), and difficulty in lubrication, in oil and gas field exploration and development drilling, especially in deep wells, high displacement wells, horizontal wells, and highly deviated wells, wear and tear are prone to occur. The application and development of titanium alloys are greatly limited. This paper introduces the research status of the common surface modification technologies of titanium alloys, such as laser cladding, magnetron sputtering, plasma spraying, micro arc oxidation, etc. It points out the improvement effect of various modification technologies on the wear resistance and high-temperature oxidation resistance of titanium alloys and discusses the advantages and disadvantages of various modification technologies. A proposed method for enhancing the wear resistance and high-temperature oxidation resistance of titanium alloys was finally introduced, and its potential for future development was investigated.

Because of its superior strength, low elastic modulus, and exceptional resistance to corrosion, titanium alloy is commonly used as a replacement for carbon steel in the construction of oil well pipes. This paper starts with the application of titanium alloy in oil well pipes in the petroleum industry, summarizes the research progress of its mechanical properties and corrosion properties in titanium alloy drill pipes and oil casing, and compares the fatigue life of several common carbon steel materials and titanium alloy in the petroleum industry. At the same time, the influence of adding metal elements and optimizing the manufacturing process on the corrosion resistance of titanium alloy is discussed. Finally, the problems that titanium alloys may face in the actual production and application process are put forward.

In this manuscript, the influence of gallium content additions of Al-Zn-In-Mg alloy was investigated through electrochemical techniques and microstructure observation in 3.5 wt% NaCl solution. The results indicated that Al-Zn-In-Mg-0.03Ga alloy has the best discharge performance among all alloys. We propose that this is due to the fact that gallium addition to the Al-4Zn-In-Mg alloy improves the discharge activity of the alloy as well as elevating its anodic efficiency. In particular, the effect of gallium addition to improve discharge activity tends to be a parabolic curve, in which there is an increase when the gallium is first added that rises to the maximum anode current efficiency of about 98.25% whenever gallium content is 0.03 wt%.

In this paper, a pragmatic technique has been developed to evaluate the erosion-corrosion behavior of three kinds of ZrN coatings (i.e., monolayer, multilayer, and gradient layers) which were deposited on AISI 420 martensitic stainless steel using an ion-assisted deposition technology. Among them, the monolayer coating refers to the coating with no change in composition and structure, the multilayer coating refers to the coating with alternating change of Zr/ZrN, and the gradient coating refers to the ZrN coating by increasing N₂ partial pressure gradually. The morphology, composition, and microhardness of these ZrN coatings were examined by means of integrating the scanning electron microscopy (SEM), X-ray diffraction (XRD), and Knoop hardness measurements, while anodic polarization tests and salt fog spray tests in a simulated industrial environment have been performed to evaluate and identify the corrosion mechanisms of these coatings. The surface microhardness and corrosion resistance of the AISI420 martensitic stainless steel is found to be significantly improved by depositing the ion-assisted deposition ZrN coatings. The study indicates that the erosion-corrosion behavior in the slurry is the result of the synergistic effect of small-angle erosion and acid solution corrosion. Three ZrN coatings hinder the slurry erosion-corrosion behavior from two aspects (i.e., erosion resistance of small-angle particles as well as corrosion resistance of the substrate), thereby significantly improving the erosion-corrosion resistance of AISI 420 stainless steel. In addition, the ZrN gradient coatings show a much better erosion-corrosion resistance than that of the monolayer/multilayer ZrN coating because they have excellent crack resistance, bearing capacity, and electrochemical performance.