Adding cement to soft soils may lead to brittle behavior and the occurrence of sudden damage. Methods to further improve the tensile and flexural properties of cemented clay are noteworthy topics. This paper mainly focuses on the effect of cement and moisture content on the strength and flexural properties of cemented clay reinforced by PVA fiber. The selected clayey soil was a kaolin with cement content of 5%, 10%, and 15% and moisture content of 50%, 56%, 63%, and 70%. The results show that the incorporation of 0.6% fiber can effectively improve the deformability of cemented clay in unconfined compression tests (UCS). The strengthening effect of fiber, as seen in the peak strength and post-peak strength of UCS, was significantly related to cement content. As the water content increased, the compressive strength of the fiber-reinforced cemented clay decreased, but its load-bearing capacity enhanced. When the cement content was 15%, the splitting tensile strength of fiber-reinforced cemented specimens increased by 11% compared to cemented soil, but the deformability of the specimens became poor. In the cement-content interval from 5% to 10%, the bending toughness was significantly improved. Sufficient cement addition ensures the enhancement of PVA fibers on strength and flexural properties of cement-stabilized clayey soil.

Pile foundations, as one of the main foundation forms for bridges and offshore wind power structures, are prone to scour pits around them under the long-term action of water flow, leading to a decrease in bearing capacity. Traditional pile foundation scour prevention measures, such as the construction of protective jetties and riprap protection, are cumbersome and ineffective. Considering the inevitable generation of a large amount of spoil in engineering construction, by optimizing the performance of cement-stabilized soil, it is expected to use the discarded spoil for pile foundation scour management. Aiming at the underwater anti-dispersive cement-stabilized soil based on kaolin, 67 sets of single-factor rotation experiments were carried out to study the effects of changes in the addition of anti-dispersive agents ethylene-vinyl acetate copolymer (EVA), hydroxypropyl methylcellulose (HPMC) from 0‰ to 1‰, cement content from 8% to 14%, and water content from 1.4 to 2 times the liquid limit on the anti-dispersion performance, fluidity, and 7d and 28d unconfined compressive strength of the cement soil. The results show that the anti-dispersive agent HPMC can maximize the anti-dispersion performance of the cement soil, with the addition increased from 0‰ to 1‰, the anti-dispersion performance of the cement soil increased by 76.1%, but the fluidity decreased by 54.0%, and the strength of the 28d age cement soil increased by about 52.9%. Anti-dispersive agents can be added to quickly improve the anti-dispersion performance of the cement soil in pile foundation scour management, but attention should also be paid to its weakening effect on the fluidity of the cement soil; the increase in water content has the greatest impact on the fluidity of the cement soil, with the water content increased from 1.4 times the liquid limit to twice the liquid limit, the fluidity increased by 80.3%; the cement content increased from 8% to 14%, the unconfined compressive strength of the cement soil increased by more than double, and the anti-dispersion performance increased by 26.8%. Based on the experimental results, the recommended mix ratio of kaolin-based cement soil for pile foundation scour repair is: 0.75‰ EVA addition, 1.6 times the liquid limit water content, 10% cement content.