Perovskite solar cells with an indium tin oxide (ITO)/SnO₂/CH₃NH₃PbI₃/Spiro-OMeTAD/2,2,2-trifluoroethanol (TFE) doped single-walled carbon nanotube (SWCNT) structure were developed by dropping TFE onto SWCNTs, which replaced the metal back electrode, and a conversion efficiency of 14.1% was achieved. Traditionally, acidic doping of the back electrode, SWCNT, has been challenging due to the potential damage it may cause to the perovskite layer. However, TFE has facilitated easy doping of SWCNT as the back electrode. The sheet resistance of the SWCNTs decreased and their ionization potential shifted to deeper levels, resulting in improved hole transport properties with a lower barrier to carrier transport. Furthermore, the Seebeck coefficient (S) increased from 34.5 μV/K to 73.1 μV/K when TFE was dropped instead of EtOH, indicating an enhancement in the behavior of p-type charge carriers. It was observed that hydrophilic substances adhered less to the SWCNT surface, and the formation of PbI₂ was suppressed. These effects resulted in higher conversion efficiency and improved solar cell performance. Furthermore, the decrease in conversion efficiency after 260 days was suppressed, showing improved durability. The study suggests that combining SWCNTs and TFEs improves solar cell performance and stability.

The advancement of efficient and stable perovskite solar cells (PSCs) increasingly depends on developing flexible, metal-free electrode architectures. Single-walled carbon nanotubes (SWCNTs) offer chemical robustness, high conductivity, and mechanical flexibility, making them promising candidates to replace brittle metal cathodes. However, pristine SWCNTs are intrinsically p-type, creating energy barriers and recombination losses in inverted (p–i–n) PSCs. Achieving stable n-type doping compatible with both SWCNTs and perovskites is therefore critical. Here, seven representative n-type dopants, small molecules (TBD and TPP), ionic salts (TBAI, TBABr, and B18C6·KCl), and polymers (PEI and PVP) were systematically investigated to elucidate their effects on doping efficiency and interfacial stability. Morphological, structural, and electronic analyses supported by DFT calculations reveal that strong bases and ionic dopants promote perovskite degradation, whereas polymeric and coordination-type dopants preserve crystallinity and surface uniformity. Among them, PEI- and TPP-doped SWCNT electrodes achieved the best device performance, with power conversion efficiencies of 9.6% and 8.1%, respectively, demonstrating efficient electron extraction and interfacial stability. These findings highlight that interfacial chemical compatibility rather than intrinsic donor strength governs the effectiveness of n-type SWCNT doping, providing rational design principles for stable, metal-free perovskite photovoltaics.