Fly ash, a type of solid waste generated in power plants, can be utilized as a catalyst carrier to enhance its value-added potential. Common methods often involve using a large amount of alkali for preprocessing, resulting in stable quartz and mullite forming silicate dissolution. This leads to an increased specific surface area and pore structure. In this study, we produced a catalyst composed of MnO_x/NiOOH supported on fly ash by directly employing nickel hydroxide and potassium permanganate to generate metal active sites over the fly ash surface while simultaneously creating a larger specific surface area and pore structure. The ozone catalytic oxidation performance of this catalyst was evaluated using sodium acetate as the target organic matter. The experimental results demonstrated that an optimal removal efficiency of 57.5% for sodium acetate was achieved, surpassing even that of MnO_x/NiOOH supported catalyst by using γ-Al₂O₃. After loading of MnO_x/NiOOH, an oxygen vacancy is formed on the surface of fly ash, which plays an indirect oxidation effect on sodium acetate due to the transformation of ozone to •O₂⁻ and •OH over this oxygen vacancy. The reaction process parameters, including varying concentrations of ozone, sodium acetate, and catalyst dosage, as well as pH value and the quantitative analysis of formed free radicals, were examined in detail. This work demonstrated that fly ash could be used as a viable catalytic material for wastewater treatment and provided a new solution to the added value of fly ash.

New flower-shaped metallophthalocyanine polymers (THB-4-M, M = Co, Cu) have been synthesized by using 1,3,5-Tri(4-hydroxyphenhyl) benzene (THB) as rigid and contorted units to control the morphology under the solvothermal method. The polymers were characterized using FT-IR, UV-vis, SEM, TGA, and XPS. These polymers were applied as heterogeneous catalysts for the chemical fixation of carbon dioxide (CO₂) to cyclic carbonates without solvent. The influence of reaction parameters and different metal centers on the catalytic performance were studied in detail. Under optimal conditions, the catalysts showed high conversion (49.9–99.0%), selectivity (over 85%), and reusability at ambient conditions (at 1 bar CO₂).