Understanding the thermal properties of zeolites is crucial for their industrial applications. This study explores the thermal stability and dehydration process of clinoptilolite using high-temperature X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR). Clinoptilolite’s thermal decomposition was monitored from 25 °C to 1200 °C, with results analyzed based on its crystal structure. Principal components analysis (PCA) of the DRIFT spectra indicated progressive water removal and dehydration upon heating, leading to the formation of hydrogen bonds. Thermogravimetric analysis (TGA) revealed a two-step endothermic weight loss: initially, physically adsorbed water was lost up to 100 °C, followed by the removal of tightly bound water and hydroxyl groups until 800 °C. Clinoptilolite remained the dominant phase up to 800 °C, after which albite and cristobalite took over. Rietveld refinement showed that the sample initially contained 70% clinoptilolite, 24% albite, and 6% cristobalite. Above 800 °C, clinoptilolite disappeared, leaving 93% albite and 7% cristobalite. FT-IR spectra changes due to water loss were evident: drying of adsorbed water occurred up to 75 °C and minimal changes were observed from 75 °C to 135 °C, followed by further dehydration until 240 °C. Complete dehydration was confirmed by the disappearance of OH stretching vibration bands by 395 °C, consistent with TGA findings.

This study investigated the structural and electrochemical characteristics of binary and quaternary systems comprising nickel, cobalt, and iron selenides. The powders were obtained via a solvothermal route. X-ray diffraction (XRD) and Raman spectroscopy revealed significant phase diversity. It was observed that increasing the proportion of d-block metals in quaternary systems enhances structural entropy, potentially leading to more homogeneous and stable structures dominated by energetically preferred components such as nickel. The electrochemical analysis indicated that the binary system exhibited a reversible redox reaction, with nickel selenide-based samples demonstrating the highest electrochemically active surface area. Quaternary systems display varying degrees of electrochemical stability. An equal contribution of nickel, cobalt, and iron appears beneficial in achieving stable electrodes. This research contributes to understanding the relationship between transition metal selenides’ structural, morphological, and electrochemical properties, providing insights into their potential applications in hydrogen generation.