Curcumin has been proven to be a potent agent in colon cancer treatment. However, its hydrophobicity and low oral bioavailability hampered its clinical application. These limitations could be improved through appropriate formulations such as using polyelectrolyte complexes (PECs). PECs were self-assembled with polycations and polyanions in polar solvents. In this study, a novel pectin-type B gelatin PEC was developed for use in curcumin formulation. At pH 4.0, natural polyanions pectin and polycations type B gelatin spontaneously formed PECs in ethanol/water solution, whereas under mimetic gastrointestinal tract (GI tract) conditions, at pH 2.0 and 8.0, pectin and type B gelatin were electrically neutralized, and the PECs swelled to allow payload release. After being transferred to pH 7.0 condition, as in the colon environment, PECs were internalized into colon carcinomas. Thus, pectin-type B gelatin PECs were successfully prepared, and their constituent ratio and drug-loading process were also optimized. The optimum particle size of the PECs was 264.0 ± 3.1 nm and they could swell as the zeta potential was altered at either pH 2.0 or 8.0. The optimum drug content and loading efficiency were 40% and 53%, respectively. At pH 2.0, curcumin was rapidly released from curcumin-loaded PECs, whereas at pH 8.0, curcumin-loaded PECs showed a sustained-release of curcumin. The bare PECs showed very low toxicity toward human normal cells, whereas curcumin-loaded PECs, after incubation at pH 2.0 for 2 h and at pH 8.0 for 4 h, induced cell cycle arrest and exhibited cytotoxic effect to HCT116 human colon cancer cells, even though these loaded PECs were pretreated with mimetic GI tract conditions. Our pectin-type B gelatin PECs were shown to be a promising oral formulation for curcumin delivery in anticancer therapy.

Stem cell-based therapy holds promise for cartilage regeneration in treating knee osteoarthritis (KOA). Injectable hydrogels have been developed to mimic the extracellular matrix (ECM) and facilitate stem cell growth, proliferation, and differentiation. However, these hydrogels face limitations such as poor mechanical strength, inadequate biocompatibility, and suboptimal biodegradability, collectively hindering their effectiveness in cartilage regeneration. This study introduces an injectable, biodegradable, and self-healing hydrogel composed of chitosan–PEG and PEG–dialdehyde for stem cell delivery. This hydrogel can form in situ by blending two polymer solutions through injection at physiological temperature, encapsulating human adipose-derived stem cells (hADSCs) during the gelation process. Featuring a 3D porous structure with large pore size, optimal mechanical properties, biodegradability, easy injectability, and rapid self-healing capability, the hydrogel supports the growth, proliferation, and differentiation of hADSCs. Notably, encapsulated hADSCs form 3D spheroids during proliferation, with their sizes increasing over time alongside hydrogel degradation while maintaining high viability for at least 10 days. Additionally, hADSCs encapsulated in this hydrogel exhibit upregulated expression of chondrogenic differentiation genes and proteins compared to those cultured on 2D surfaces. These characteristics make the chitosan–PEG/PEG–dialdehyde hydrogel–stem cell construct suitable for direct implantation through minimally invasive injection, enhancing stem cell-based therapy for KOA and other cell-based treatments.

In this study, for the first time, we precisely assembled the poly-γ-benzyl-l-glutamate and an amphiphilic copolymer d-α-tocopherol polyethylene glycol succinate into a mixed micellar system for the embedment of the anticancer drug doxorubicin. Importantly, the intracellular drug-releasing behaviors could be controlled by changing the secondary structures of poly-γ-benzyl-l-glutamate via the precise regulation of the buffer’s pH value. Under neutral conditions, the micellar architectures were stabilized by both α-helix secondary structures and the microcrystalline structures. Under acidic conditions (pH 4.0), the interior structures transformed into a coil state with a disordered alignment, inducing the release of the loaded drug. A remarkable cytotoxicity of the Dox-loaded mixed micelles was exhibited toward human lung cancer cells in vitro. The internalizing capability into the cancer cells, as well as the intracellular drug-releasing behaviors, were also identified and observed. The secondary structures containing Dox-loaded mixed micelles had an outstanding antitumor efficacy in human lung cancer A549 cells-bearing nude mice, while little toxicities occurred or interfered with the hepatic or renal functions after the treatments. Thus, these pH-tunable α-helix-containing mixed micelles are innovative and promising for controlled intracellular anticancer drug delivery.