This study was conducted to investigate the impact of hot and dry environments under different curing conditions on the properties of high‐strength concrete. The concrete samples were prepared at a room temperature of 20°C and cured under different curing conditions. Some specimens underwent standard curing from 24 h after casting until the day of testing. Some specimens underwent steam curing in a dry oven at 30°C and 50°C after casting until the day of testing. Other specimens were cured for 3, 7, 21, and 28 days in water and then placed in a dry oven at 30°C and 50°C and tested at the age of 28 days, except for the specimens that were cured for 28 days, which were tested at the age of 31 days, to study the effect of curing period on the strength of concrete exposed to dry and hot environments after moist curing. The effects of hot and dry environments on high‐strength concrete with different water/binder ratios (0.30, 0.35, and 0.40), using (30%) fly ash for all mixes, and (0%, 5%, and 10%) silica fume with the binder (450, 480, and 520 kg), respectively, were separately investigated, and the effects of curing under different conditions were evaluated by measuring the compressive strength, flexural strength, microhardness, and chloride diffusion and by assessing the concretes’ microstructure. The relationships between these properties were presented. A good agreement was noted between the concrete compressive strength and concrete properties at different temperatures, curing periods, and curing methods.

A comprehensive program of experiments consisting of compression, uniaxial compression, direct shear, flexural as well as splitting tensile and air permeability tests were performed to analyse the effect of the level of fibre dosage and the water–cement ratio on the physical properties of hybrid fibre-reinforced concrete (HFRC). Two types of fibres were studied in terms of their effect on the properties of HFRC. The results indicated that the mechanical properties of concrete were significantly improved by increasing the fibre content. However, increasing the percentage fibre content past a certain peak performance limit (0.9% glass fibre (GF) and 0.45% polypropylene fibre (PPF)) led to a decrease in strength compared to reference mixes. Additionally, the incorporation of hybrid fibres yielded an increase in air permeability in the tested specimens. The results showed that the strength-related properties of HFRC were superior to the properties of single fibre-reinforced concrete.