The photodynamic activities of the free-base 5,10,15,20-tetrakis(4-methoxyphenyl)porphyrin (TMP) and their metal complexes with zinc(II) (ZnTMP), copper(II) (CuTMP) and cadmium(II) (CdTMP) have been compared in two systems: reverse micelle of n-heptane/sodium bis(2-ethylhexyl)sulfosuccinate/water bearing photooxidizable substrates and Hep-2 human larynx carcinoma cell line. The quantum yields of singlet molecular oxygen, O2(1Δg), production (ΦΔ) of TMP, ZnTMP and CdTMP in tetrahydrofuran, were determined yielding values of 0.65, 0.73 and 0.73, respectively, while O2(1Δg) formation was not detected for CuTMP. In the reverse micellar system, the amino acid l-tryptophan (Trp) was used as biological substrate to analyze the O2(1Δg)-mediated photooxidation. The observed rate constants for Trp photooxidation (kobsTrp) were proportional to the sensitizer quantum yield of O2(1Δg). A value of ∼2 × 107 s−1 M−1 was found for the second-order rate constant of Trp (krTry) in this system. The response of Hep-2...

Polyaniline nanoparticles (PANI-NPs) were easily obtained applying the solvent displacement method by using N-methylpyrrolidone (NMP) as good solvent and water as poor solvent . Different polymers such as polyvinylpyrrolidone (PVP), chondroitin sulfate (ChS), polyvinyl alcohol (PVA), and polyacrylic acid (PAA) were used as stabilizers. Dynamic light scattering and scanning electron microscopy corroborated the size and morphology of the formed NPs. It was demonstrated that the size of nanoparticles could be controlled by setting the concentration of PANI in NMP, the NMP to water ratio, and the stabilizer’s nature. The functionalization and fluorescence of NPs were checked by spectroscopic techniques. Since polyaniline show only weak intrinsic luminescence, fluorescent groups were linked to the polyaniline chains prior to the nanoparticle formation using a linker. Polyaniline chains were functionalized by nucleophilic addition of cysteamine trough the thiol group thereby incorporating pendant primary aliphatic amine groups to the polyaniline backbone. Then, dansyl chloride (DNS-Cl), which could act as an extrinsic chromophore, was conjugated to the amine pendant groups. Later, the functionalized polyaniline was used to produce nanoparticles by solvent displacement. The optical and functional properties of fluorescent nanoparticles (F-PANI-NPs) were determined. F-PANI-NPs in the conductive state (pH < 4) are able to absorb near infrared radiation (NIR) creating a photothermal effect in an aqueous medium. Thus, multifunctional nanoparticles are obtained. The application of NIR on a F-PANI-NPs dispersion in contact with Pseudomonas aeruginosa causes bacterial death. Therefore, the F-PANI-NPs could be tracked and applied to inhibit different diseases caused by pathogenic microorganisms and resistant to antibiotics as well as a new disinfection method to surgical materials.