High-strength dissimilar aluminum alloys are difficult to connect by fusion welding, while they can be successfully joined by friction stir welding (FSW). However, the asymmetrical deformation and heat input that occur during FSW result in the formation of a heterogeneous microstructure in their welded zone. In this work, the grain structure and texture evolution in the bottom zones of dissimilar FSW AA2024-T351 and AA7075-T651 joints at different welding speeds (feeding speeds) were quantitatively investigated. The results indicated that dynamic recrystallization occurs in the bottom zones of dissimilar FSW joints, and equiaxed grains with low grain sizes are formed at the welding speed of 60–240 mm/min. A high fraction of the recrystallized grains were generated in the bottom zones of the joints at a low welding speed, while a high fraction of the substructured grains are produced at a high welding speed. Different types of shear textures are produced in the bottom zones of the joints; the number fraction of shear texture types depends on different welding speeds. This study helps to understand the mechanism of microstructure homogenization in dissimilar FSW joints and provides a basis for further improving the microstructure of the welded zone for engineering applications.

Friction-stir-welded dissimilar AA2024/AA7075 joints have an apparent influence on grain and texture development at the weld interface due to differences in physical and chemical properties between the two aluminum alloys. In this work, the effect of tool shoulder profile on grain structure and texture evolution in the center interface zone (CIZ) and bottom interface zone (BIZ) of dissimilar AA2024/AA7075 joints were quantitatively studied by electron back-scattering diffraction (EBSD). The results indicate that abundant fine and coarse equiaxial grains are produced in the CIZ and BIZ of the joints produced with a concentric circle shoulder (CCS) and three-helix shoulder (THS), and the average grain size of the BIZ is lower than that of the CIZ for the same CCS or THS joint. A higher degree of recrystallization occurs in the CIZ of the joint with a CCS than that of the joint with a THS, while a similar degree of recrystallization is presented in the BIZ of the two joints. For the distribution of local misorientation angle between the two sides of the interface in the same CCS or THS joint, the CIZ manifests relatively uniform behavior, while the BIZ presents the characteristics of uneven distribution. Tool shoulder profile has a significant impact on the texture components at the weld interface, which results in different types of shear textures generated in the CIZ and BIZ of the two joints. It is beneficial to make out the microstructural evolution mechanism at the weld interface in dissimilar FSW joints for engineering applications in this study.