Thermoplastic composite organosheets (OSs) are increasingly recognized as a viable solution for automotive and aerospace structures, offering a range of benefits including cost-effectiveness through high-rate production, lightweight design, impact resistance, formability, and recyclability. This study examines the impact response, post-impact strength evaluation, and hot-pressing repair effectiveness of woven glass fiber nylon composite OSs across varying impact energy levels. Experimental investigations involved subjecting composite specimens to impact at varying energy levels using a drop-tower test rig, followed by compression-after-impact (CAI) tests. The results underscore the exceptional damage tolerance and improved residual compressive strength of the OSs compared to traditional thermoset composites. This enhancement was primarily attributed to the matrix’s ductility, which mitigated transverse crack propagation and significantly increased the amount of absorbed energy. To mitigate impact-induced damage, a localized hot-pressing repair approach was developed. This allowed to restore the post-impact strength of the OSs to pristine levels for impact energies below 40 J and by 83.6% for higher impact energies, when OS perforation was observed. The measured levels of post-repair strength demonstrate a successful restoration of OS strength over a wide range of impact energies, and despite limitations in achieving complete strength recovery above 40 J, hot-pressing repair emerges as a promising strategy for ensuring the longevity of thermoplastic composites through repairability.

Fiber tow-gaps and overlaps formed during the Automated Fiber Placement (AFP) process pose a significant challenge by introducing non-uniform composite morphologies, often characterized by resin-rich regions and fiber waviness. These defects occur as deposited fibers sink into the gap regions during consolidation, with gap geometry determined during path planning. Such morphological inconsistencies can compromise structural reliability by initiating premature failure, particularly through localized out-of-plane waviness and resin accumulation. This study investigates the integration of high melting temperature thermoplastic veils, specifically polyetherimide (PEI), into fiber tow-gaps as a method to prevent ply sinking and reduce fiber waviness on both internal and external surfaces of the laminate. The PEI veils also serve to reinforce resin-rich regions by forming an interpenetrated network of high fracture toughness material within the brittle epoxy matrix. Tensile tests conducted on cross-ply laminates containing staggered gaps demonstrated that the inclusion of PEI veils modified the failure mode. The results suggest that the selective placement of thermoplastic veils within tow-gaps during AFP offers a viable strategy to mitigate manufacturing-induced non-uniform morphologies.