Poly-L-Lactic acid (PLLA) blended with chitosan and collagen was used to fabricate a conduit for blood vessel engineering through an electrospinning process. Various concentrations of chitosan were used in the blend in order to study its effect on the morphology, chemical bond, tensile strength, burst pressure, hemocompatibility, and cell viability (cytotoxicity) of the tube.In vitro assessments indicated that addition of chitosan-collagen could improve cell viability and hemocompatibility. Best results were demonstrated by the conduit with 10% PLLA, 0.5% chitosan, and 1% collagen. Tensile strength reached 2.13 MPa and burst pressure reached 2593 mmHg, both values that are within the range value of native blood vessel. A hemolysis percentage of 1.04% and a cell viability of 86.2% were obtained, meeting the standards of high hemocompatibility and low cytotoxicity for vascular graft material. The results are promising for further development toward vascular graft application.

Human immunodeficiency virus (HIV) infection and acquired immune deficiency syndrome (AIDS) cause serious health problems and have an impact on the Indonesian economy. In addition, the rapid epidemic growth of HIV is continuing in Indonesia. Commercial sex plays a significant role in the spread of HIV; therefore, in order to reveal the current HIV prevalence rate among commercial sex workers (CSWs), we conducted an epidemiological study on HIV infection among CSWs residing in Surabaya, the capital of East Java province of Indonesia with large communities of CSWs. The prevalence of HIV infection among 200 CSWs was studied. In addition, the subtype of HIV type 1 (HIV-1) and the prevalence of other blood-borne viruses, hepatitis B virus (HBV), hepatitis C virus (HCV) and GB virus C (GBV-C), were studied. The prevalence rates of HIV, hepatitis B core antibody, hepatitis B surface antigen, anti-HCV antibodies and anti-GBV-C antibodies were 11%, 64%, 4%, 0.5% and 0% among CSWs involved in this study, respectively. HIV-1 CRF01_AE viral gene fragments were detected in most HIV-positive samples. In addition, most CSWs showed low awareness of sexually transmitted diseases and had unprotected sex with their clients. The HIV prevalence rate among CSWs was significantly higher than that among the general population in Indonesia (0.2–0.4%). In addition, CSWs were at a high risk of exposure to HBV, although chronic HBV infection was less frequently established. Our results suggest the necessity of efficient prevention programs for HIV and other blood-borne viral infections among CSWs in Surabaya, Indonesia.

Thirty percent of global mortalities are caused by cardiovascular disease, and 54% of the aforementioned amount is instigated by ischemic heart disease that triggered myocardial infarction. Myocardial infarction is due to blood flow cessation in certain coronary arteries that causes lack of oxygen (ischemia) and stimulates myocardial necrosis. One of the methods to treat myocardial infarction consists in injecting cells or active biomolecules and biomaterials into heart infarction locations. This study aimed to investigate the characteristics of a collagen–chitosan-based hydrogel with variations in its chitosan composition. The prepared hydrogels contained thymosin β4 (Tβ4), a 43-amino acid peptide with angiogenic and cardioprotective properties which can act as a bioactive molecule for the treatment of myocardial infarction. A morphological structure analysis showed that the hydrogels lacked interconnecting pores. All samples were not toxic on the basis of a cytotoxicity test. A histopathological anatomy test showed that the collagen–chitosan–thymosin β4 hydrogels could stimulate angiogenesis and epicardial heart cell migration, as demonstrated by the evaluation of the number of blood vessels and the infiltration extent of myofibroblasts.

Synthetic scaffolding for bone tissue engineering (BTE) has been widely utilized. The scaffold for BTE requires sufficient porosity as a template for bone cell development and growth so that it can be used in the treatment of bone defects and fractures. Nevertheless, the porosity significantly influences the compressive strength of the scaffold. Hence, controlling the porosity is a pivotal role to obtain a proper scaffold for practical BTE application. Herein, we fabricated the nanocomposite-based scaffold utilizing nano-hydroxyapatite (n-HA). The scaffold was prepared in combination with chitosan (Ch) and carboxymethyl cellulose (CMC). The ratios of n-HA, Ch, and CMC used were 40:60:0, 40:55:5, 40:50:10, 40:45:15, and 40:40:20, respectively. By controlling the Ch and CMC composition, we can tune the porosity of the nanocomposite. We found that the interpolation of the CMC prevails, as a crosslinker reinforces the nanocomposite. In addition, the binding to Ch enhanced the compressive strength of the scaffold. Thermal characteristics revealed the coefficient of thermal expansion decreases with increasing CMC content. The nanocomposite does not expand at 25–75 °C, which is suitable for human body temperature. Therefore, this nanocomposite-based scaffold is feasible for BTE application.

In Indonesia, breast cancer is noted as the most common cancer in women. Accordingly, this research was conducted to synthesize biofilm from bacterial cellulose by adding ethanol extract of mangosteen peel. The pellicle of bacterial cellulose was soaked in a 100 mL ethanol solution of mangosteen peel extract varied by 0.5%, 1%, 1.5%, and 2% v/v. The samples were characterized using the SEM, FTIR, and MTT Assay using the T47D breast cancer cells. The results using the SEM showed the thickness of the bacterial cellulose biofilm samples was 5.63 μm, while the 2% v/v thickness of the bacterial cellulose of the extract of mangosteen peel biofilm samples was 12.2 μm. The FTIR results showed a weak interaction between the O-H groups of the microbial cellulose and the C=C functional group in the phenolic compounds of the mangosteen peel extract. Based on the MTT Assay test results using the T47D breast cancer cells, the highest percentage of cell death result was 25.47% on the 2% v/v bacterial cellulose of the mangosteen peel extract samples. The Garcinia mangostana extracts added in the bacterial cellulose biofilms still required optimal concentrations in order to become potential killing mechanism for the T47D breast cancer cells.