For the large-scale sustainable implementation of polymer electrolyte membrane fuel cells in vehicles, high-performance electrocatalysts with low platinum consumption are desirable for use as cathode material during the oxygen reduction reaction in fuel cells. Here we report a carbon black-supported cost-effective, efficient and durable platinum single-atom electrocatalyst with carbon monoxide/methanol tolerance for the cathodic oxygen reduction reaction. The acidic single-cell with such a catalyst as cathode delivers high performance, with power density up to 680 mW cm⁻² at 80 °C with a low platinum loading of 0.09 mg_Pt cm⁻², corresponding to a platinum utilization of 0.13 g_Pt kW⁻¹ in the fuel cell. Good fuel cell durability is also observed. Theoretical calculations reveal that the main effective sites on such platinum single-atom electrocatalysts are single-pyridinic-nitrogen-atom-anchored single-platinum-atom centres, which are tolerant to carbon monoxide/methanol, but highly active for the oxygen reduction reaction.

The classical strong metal–support interaction between TiO₂and IB metals was demonstrated.

Transition metal phosphides (TMPs) have recently emerged as a new class of pre-catalysts that can efficiently catalyze the oxygen evolution reaction (OER). However, how the OER activity of TMPs varies with the catalyst composition has not been systematically explored. Here, we report the alkaline OER electrolysis of a series of nanoparticulate phosphides containing different equimolar metal (M = Fe, Co, Ni) components. Notable trends in OER activity are observed, following the order of FeP < NiP < CoP < FeNiP < FeCoP < CoNiP < FeCoNiP, which indicate that the introduction of a secondary metal(s) to a mono-metallic TMP substantially boosts the OER performance. We ascribe the promotional effect to the enhanced oxidizing power of bi- and tri-metallic TMPs that can facilitate the formation of MOH and chemical adsorption of OH⁻ groups, which are the rate-limiting steps for these catalysts according to our Tafel analysis. Remarkably, the tri-metallic FeCoNiP pre-catalyst exhibits exceptionally high apparent and intrinsic OER activities, requiring only 200 mV to deliver 10 mA cm⁻² and showing a high turnover frequency (TOF) of ≥0.94 s⁻¹ at the overpotential of 350 mV.

In this article, we for the first time report the synthesis and electrocatalytic properties of ruthenium cobalt phosphide hybrid clusters for the hydrogen evolution reaction (HER). Two types of catalysts are investigated: wet chemical reduction of Ru³⁺ on pre-formed cobalt phosphide (CoP) nanoparticles results in ruthenium–cobalt phosphide side-by-side structures (Ru/CoP); while phosphorizing chemically reduced RuCo alloy leads to the formation of hybrid ruthenium cobalt phosphide (RuCoP) clusters. Compared to pristine Ru clusters, both Ru/CoP and RuCoP show significantly improved HER performance in both acidic and alkaline solutions. In particular, the hybrid RuCoP clusters demonstrate a considerably low overpotential (η₁₀) of 11 mV at −10 mA cm⁻² and a high turnover frequency (TOF) of 10.95 s⁻¹ at η = 100 mV in 0.5 M H₂SO₄. Even in 1.0 M KOH the excellent HER activity of the RuCoP clusters remains, with a very low η₁₀ of 23 mV and exceptionally high TOF value of 7.26 s⁻¹ at η = 100 mV. Moreover, the RuCoP catalysts can sustain galvanostatic electrolysis in both acidic and alkaline solutions at −10 mA cm⁻² for 150 h with little degradation, showing better catalytic stability than the state-of-the-art commercial Pt/C catalysts. Our density functional theory (DFT) calculations indicate that the RuCoP hybrid exhibits a hydrogen adsorption energy very close to that of Pt and water and –OH adsorption energies distinct from pristine Ru, which reasonably explain the experimentally observed excellent HER activities and highlight the importance of synergistic coupling with cobalt phosphide to boost the HER performance of ruthenium.