The dual extrusion electrospinning technique was used to fabricate multilayered 3D scaffolds by stacking microfibrous meshes of poly(lactic acid-co-glycolic acid) (PLGA) in alternate fashion to micro/nano mixed fibrous meshes of PLGA and collagen. To fabricate the multilayered scaffold, 35 wt% solution of PLGA in THF-DMF binary solvent (3:1) and 5 wt% solution of collagen in hexafluoroisopropanol (HFIP) with and without hydroxyapatite nanorods (nHA) were used. The dual and individual electrospinning of PLGA and collagen were carried out at flow rates of 1.0 and 0.5 mL/h, respectively, at an applied voltage of 20 kV. The density of collagen fibers in multilayered scaffolds has controlled the adhesion, proliferation, and osteogenic differentiation of MC3T3-E1 cells. The homogeneous dispersion of glutamic acid-modified hydroxyapatite nanorods (nHA-GA) in collagen solution has improved the osteogenic properties of fabricated multilayered scaffolds. The fabricated multilayered scaffolds were characterized using FT-IR, X-ray photoelectron spectroscopy, and transmission electron microscopy (TEM). The scanning electron microscopy (FE-SEM) was used to evaluate the adhesion and spreads of MC3T3-E1 cells on multilayered scaffolds. The activity of MC3T3-E1 cells on the multilayered scaffolds was evaluated by applying MTT, alkaline phosphatase, Alizarin Red, von Kossa, and cytoskeleton F-actin assaying protocols. The micro/nano fibrous PLGA-Col-HA scaffolds were found to be highly bioactive in comparison to pristine microfibrous PLGA and micro/nano mixed fibrous PLGA and Col scaffolds.

Despite the susceptibility to frequent intrinsic and extrinsic injuries, especially in the inner zone, the meniscus does not heal spontaneously owing to its poor vascularity. In this study, the effect of platelet-rich plasma (PRP), containing various growth factors, on meniscal mechanisms was examined under normal and post-traumatic inflammatory conditions. Isolated primary meniscal cells of New Zealand white (NZW) rabbits were incubated for 3, 10, 14 and 21 days with PRP(−), 10% PRP (PRP(+)), IL(+) or IL(+)PRP(+). The meniscal cells were collected and examined using reverse-transcription polymerase chain reaction (RT-PCR). Culture media were examined by immunoblot analyses for matrix metalloproteinases (MMP) catabolic molecules. PRP containing growth factors improved the cellular viability of meniscal cells in a concentration-dependent manner at Days 1, 4 and 7. However, based on RT-PCR, meniscal cells demonstrated dedifferentiation, along with an increase in type I collagen in the PRP(+) and in IL(+)PRP(+). In PRP(+), the aggrecan expression levels were lower than in the PRP(−) until Day 21. The protein levels of MMP-1 and MMP-3 were higher in each PRP group, i.e., PRP(+) and IL(+)PRP(+), at each culture time. A reproducible 2-mm circular defect on the meniscus of NZW rabbit was used to implant fibrin glue (control) or PRP in vivo. After eight weeks, the lesions in the control and PRP groups were occupied with fibrous tissue, but not with meniscal cells. This study shows that PRP treatment of the meniscus results in an increase of catabolic molecules, especially those related to IL-1α-induced inflammation, and that PRP treatment for an in vivo meniscus injury accelerates fibrosis, instead of meniscal cartilage.

Porous calcium phosphate ceramics are used in orthopedic and craniofacial applications to treat bone loss, or in dental applications to replace missing teeth. The implantation of these materials, however, does not induce stem cell differentiation, so suitable additional materials such as porous calcium phosphate discs are needed to influence physicochemical responses or structural changes. Rabbit adipose-derived stem cells (ADSC) and mouse osteoblastic cells (MC3T3-E1) were evaluated in vitro by the MTT assay, semi-quantitative RT-PCR, and immunoblotting using cells cultured in medium supplemented with extracts from bioceramics, including calcium metaphosphate (CMP), hydroxyapatite (HA) and collagen-grafted HA (HA-col). In vivo evaluation of the bone forming capacity of these bioceramics in rat models using femur defects and intramuscular implants for 12 weeks was performed. Histological analysis showed that newly formed stromal-rich tissues were observed in all the implanted regions and that the implants showed positive immunoreaction against type I collagen and alkaline phosphatase (ALP). The intramuscular implant region, in particular, showed strong positive immunoreactivity for both type I collagen and ALP, which was further confirmed by mRNA expression and immunoblotting results, indicating that each bioceramic material enhanced osteogenesis stimulation. These results support our hypothesis that smart bioceramics can induce osteoconduction and osteoinduction in vivo, although mature bone formation, including lacunae, osteocytes, and mineralization, was not prominent until 12 weeks after implantation.

Flash sintering is a novel and emerging route for sintering ceramics within a few seconds, even under pressure-less conditions. In the current study, hydroxyapatite (HA) was fully densified by flash sintering at a furnace temperature of 1020°C. Flash sintering with constant electric fields of 750 and 1000 V cm⁻¹ reduced the grain growth rate significantly compared to that sintered in the absence of an electric field at 1400°C. The microstructure of HA consolidated by flash sintering was compared with that of the without electric field sintered samples. The flash-sintered samples showed smaller grains (160 ∼ 320 nm) than the without electric field sintered samples (∼15 µm). The samples with a higher applied electric field showed slightly better densification than those with the lower field by flash sintering. Overall, the electric flash reduces the sintering temperature effectively and decreases the holding time to densify highly insulating ceramics, such as HA.

Bone grafts used in alveolar bone regeneration can be categorized into autografts, allografts, xenografts, and synthetic bones, depending on their origin. The purpose of this study was to evaluate the effect of a commercialized octacalcium phosphate (OCP)-based synthetic bone substitute material (Bontree^®) in vitro, in vivo, and in clinical cases. Material characterization of Bontree^® granules (0.5 mm and 1.0 mm) using scanning electron microscopy and X-ray diffraction showed that both 0.5 mm and 1.0 mm Bontree^® granules were uniformly composed mainly of OCP. The receptor activator of NF-κB ligand (RANKL) and alkaline phosphatase (ALP) activities of MG63 cells were assessed and used to compare Bontree^® with a commercial biphasic calcium phosphate ceramic (MBCP+^TM). Compared with MBCP+^TM, Bontree^® suppressed RANKL and increased ALP activity. A rabbit tibia model used to examine the effects of granule size of Bontree^® grafts showed that 1.0 mm Bontree^® granules had a higher new bone formation ability than 0.5 mm Bontree^® granules. Three clinical cases using Bontree^® for ridge or sinus augmentation are described. All eight implants in the three patients showed a 100% success rate after 1 year of functional loading. This basic research and clinical application demonstrated the safety and efficacy of Bontree^® for bone regeneration.