Polymer blending techniques enable the tailoring of desired properties for diverse applications. This study investigates the effect of PMMA content on the thermomechanical, chemical, mechanical, and fatigue life properties of PC/ABS/PMMA (polycarbonate/acrylonitrile–butadiene–styrene/polymethylmethacrylate) ternary blends. To this end, various characterization analyses, as well as tensile, impact, and fatigue tests, were conducted. The results indicate that the viscoelastic modulus improves with increasing PMMA content in ternary blends. Furthermore, PC/ABS/PMMA blends exhibit an immiscible phase morphology. The elastic modulus, yield strength, and tensile strength increase with higher PMMA content, while the elongation at break and impact strength decrease. Fatigue strength and the fatigue strength exponent were found to vary nonlinearly with PMMA content. Compared to PC/ABS blends, PC/ABS/PMMA blends demonstrated improvements of approximately 12% to 58% and 26% to 117% in hysteresis energy and the dynamic elastic modulus, respectively. Additionally, fatigue life cycles improved by 5% to 11% at low stress amplitudes. This experimental study provides comprehensive insight into the complex interplay among the chemical, thermomechanical, mechanical, and fatigue properties of ternary PC/ABS/PMMA blends, highlighting their potential for applications requiring balanced or tailored structural and material characteristics.

Severe plastic deformation (SPD) techniques are prospective ones having ability for desirable high mechanical properties to be achieved without any chemical change in metals. Equal-channel angular pressing (ECAP), one of SPD techniques, was used to obtain ultra-high mechanical compressive response of stainless steel pyramidal lattice core. For this purpose, the stainless steel 304 L samples were processed by ECAP at 500 °C. Then, it was sliced into struts and built lattice core after bending processes. At the compression tests, the ECAP lattice core has huge mechanical properties, at nearly two times collapse load and energy absorption values.