Low-concentrated colloidal chitosan systems undergoing a thermally induced sol–gel phase transition are willingly studied due to their potential use as minimally invasive injectable scaffolds. Nevertheless, instrumental injectability tests to determine their clinical utility are rarely performed. The aim of this work was to analyze the flow phenomenon of thermosensitive chitosan systems with the addition of disodium β-glycerophosphate through hypodermic needles. Injectability tests were performed using a texture analyzer and hypodermic needles in the sizes 14G–25G. The rheological properties were determined by the flow curve, three-interval thixotropy test (3ITT), and Cox–Merz rule. It was found that reducing the needle diameter and increasing its length and the crosshead speed increased the injection forces. It was claimed that under the considered flow conditions, there was no need to take into account the viscoelastic properties of the medium, and the model used to predict the injection force, based solely on the shear-thinning nature of the experimental material, showed very good agreement with the experimental data in the shear rate range of 200–55,000 s⁻¹. It was observed that the increase in the shear rate value led to macroscopic structural changes of the chitosan sol caused by the disentangling and ordering of the polysaccharide chains along the shear field.

Chitosan colloidal systems, created by dispersing in aqueous solutions of hydrochloric acid, with and without the addition of disodium β-glycerophosphate (β-NaGP), were prepared for the investigation of forming mechanisms of chitosan hydrogels. Three types of chitosan were used in varying molecular weights. The impacts of the charge and shape of the macromolecules on the phase transition process were assessed. The chitosan system without the addition of β-NaGP was characterized by stiff and entangled molecules, in contrast to the chitosan system with the addition of β-NaGP, wherein the molecules adopt a more flexible and disentangled form. Differences in molecules shapes were confirmed using the Zeta potential and thixotropy experiments. The chitosan system without β-NaGP revealed a rapid nature of phase transition—consistent with diffusion-limited aggregation (DLA). The chitosan system with β-NaGP revealed a two-step nature of phase transition, wherein the first step was consistent with reaction-limited aggregation (RLA), while the second step complied with diffusion-limited aggregation (DLA).

In this article, properties of thermosensitive chitosan hydrogels prepared with the use of chitosan chloride with β-glycerophosphate disodium salt pentahydrate enriched with calcium glycerophosphate are presented and compared with chitosan hydrogels with β-glycerophosphate disodium salt pentahydrate. The study is focused on the determination of hydrogel structure and biological testing of hydrogels with human osteoblasts line Saos-2. The structure of gels was visualized by scanning electron microscopy and was investigated by infrared spectroscopy. The crystallinity of gel structure was determined by X-ray diffraction analysis and thermal effects were determined using differential scanning calorimetry thermograms.