Background: This study aimed to evaluate the biological behavior of a novel implant design incorporating decompressive cervical blades. Hence, the aim of the present study was to evaluate the healing outcomes in cortical regions where decompressive protocols were implemented using implants equipped with blades and installed applying a bicortical anchorage. Materials and Methods: Blades with varying diameters were integrated into the coronal portion of the implant to prepare the cortical region of rabbit tibiae. The blade diameters differed from the implant collar by the following amounts: control group (0 µm), +50 µm, and +200 µm. Results: No marginal bone loss was detected. Instead, all implants exhibited new bone formation in the coronal region. Complete closure was observed in the CG-0 group, as well as in the TG-50 and TG-200 groups, despite the presence of marginal gaps without primary bone contact at installation. In the apical region, most implants breached the cortical layer. Nevertheless, new bone formation in this region completely closed the osteotomy, effectively isolating the internal environment of the tibia from the external. Conclusions: The use of a blade incorporated into the implant body enabled precise preparation of the cortical layer, allowing for controlled decompression in the targeted area. This technique resulted in optimal osseointegration with no loss of marginal bone, and complete restoration of marginal gaps ranging from 0 µm to 200 µm.

Background: This study stands as a pioneer in the histological evaluation of the biological behavior of a novel implant design featuring decompressive cervical blades. Hence, the aim of the present study was to evaluate the healing outcome in cortical regions at where decompressive protocols were adopted using implants equipped with blades. Materials and methods: Blades with varying diameters were integrated into the coronal portion of the implant to prepare the cortical region of rabbit tibiae. The blade diameters differed from the implant collar by the following amounts: control group (0 µm), +50 µm, and +200 µm. Results: No marginal bone loss was detected. Instead, all implants exhibited new bone formation in the coronal region. Complete closure was observed in the CG-0 group, as well as in the TG-50 and TG-200 groups, despite the presence of marginal gaps without primary bone contact at installation. In the apical region, most implants breached the cortical layer. Nevertheless, new bone formation in this region completely closed the osteotomy, effectively isolating the internal environment of the tibia from the external. Conclusions: The use of a blade attached to the implant body enabled precise preparation of the cortical layer, allowing for controlled decompression in the targeted area. This technique resulted in optimal osseointegration with no loss of marginal bone, and complete restoration of marginal gaps ranging from 0 µm to 200 µm.

Background: Osseointegrated implants are essential for rehabilitating edentulous patients, but critical bone defects remain challenging. Guided bone regeneration (GBR) with barrier membranes is an effective approach. This study evaluated a 3D printed membrane made from acrylated epoxidized soybean oil (AESO) combined with a xenogeneic graft for GBR in critical-size defects. Methods: Forty-eight male Sprague Dawley rats (150 g) were assigned to four groups: a negative control group (NC, blood clot only), a positive control group (PC, biomaterial without membrane), a negative test group (NT, blood clot with membrane), and a positive test group (PT, biomaterial with membrane). Results: The PT group showed the highest bone volume and superior bone maturation compared to the other groups. Bone quality parameters (Tb.N, Tb.Th) indicated enhanced maturation in the groups using the membrane. A histological analysis confirmed centripetal bone formation. Conclusion: The AESO-based membrane provided mechanical support and controlled resorption, addressing collagen membrane limitations. Its combination with the GTO^® graft material enhanced osteoconduction, bone formation, and bone quality, highlighting its potential for complex bone defect reconstructions.