Numerous in vivo, in vitro and clinical studies report on beneficial effects of strontium with respect to increased bone growth. Based on this knowledge the aim of this study was to evaluate early and late osseointegration stages of functionalized titanium implants showing sustained release of strontium (Sr) and further investigate its potential systemic effect. Strontium functionalized (Ti-Sr-O) and Grade 4 (Control) titanium implants were inserted in the femoral condyle of New Zealand White rabbits. The Ti-Sr-O coating was characterized using Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectrometry (EDX) for structure, coating thickness and chemical composition. Inductively Coupled Plasma Atomic Emission Spectrometry (ICP-AES) was used to evaluate released strontium in vitro while Atomic Absorption Spectrometry (AAS) was utilized to monitor serum levels of strontium and calcium. Additionally, histological and tomographic analysis of bone-to-implant contact (BIC%) and bone formation (BF%) was performed, following implantation periods of two or twelve weeks, respectively. Median values for BIC% for Ti-Sr-O revealed significant differences within the two- and twelve-week observation periods, while exceeding BF% was discovered especially after twelve weeks when performing the histological evaluation. The results from the micro-computed tomography (µ-CT) showed no significant differences, when comparing the experimental groups. AAS measurements did not indicate a systemic effect by the local strontium release. Within the limitations of the study, it was shown that a Ti-Sr-O coating with sustained release characteristics of strontium, accelerates bone apposition and represents a potential potent surface modification for endosseous medical implant devices. This study presents first data with respect to early and late in vivo response on a strontium functionalized titanium surface comprising a nanotopography manufactured by a magnetron sputtering process. We investigated different osseointegration stages of screw-shaped implants with dental implant geometries in a rabbit femur model observing beneficial effects of the functionalized surface on bone-to-implant contact and bone formation caused by tailored release of the bone anabolic strontium. Histomorphometrical data revealed that a functionalized titanium surface with controlled liberation of strontium accelerates osseointegration while spectrometry measurements did not indicate a potential systemic effect of this osteoinductive agent and could thus have impact on modifications of medical implant devices.

Computer-aided design and computer-aided manufacturing (CAD/CAM) denture base manufacturers claim to produce their resin pucks under high heat and pressure. Therefore, CAD/CAM dentures are assumed to have enhanced mechanical properties and, as a result, are often produced with lower denture base thicknesses than conventional, manually fabricated dentures. The aim of this study was to investigate if commercially available CAD/CAM denture base resins have more favourable mechanical properties than conventionally processed denture base resins. For this purpose, a series of three-point bending tests conforming to ISO specifications were performed on a total of 80 standardised, rectangular CAD/CAM denture base resin specimens from five different manufacturers (AvaDent, Baltic Denture System, Vita VIONIC, Whole You Nexteeth, and Wieland Digital Dentures). A heat-polymerising resin and an autopolymerising resin served as the control groups. The breaking load, fracture toughness, and the elastic modulus were assessed. Additionally, the fracture surface roughness and texture were investigated. Only one CAD/CAM resin showed a significantly increased breaking load. Two CAD/CAM resins had a significantly higher fracture toughness than the control groups, and all CAD/CAM resins had higher elastic moduli than the controls. Our results indicate that CAD/CAM denture base resins do not generally have better mechanical properties than manually processed resins. Therefore, the lower minimum denture base thicknesses should be regarded with some caution.

Purpose: Studies have shown that strontium-doped medical applications benefit bone metabolism leading to improved bone healing and osseointegration. Based on this knowledge, the aim of the study was to evaluate the performance of an implant surface, functionalized by a physical vapor deposition (PVD) coating (Ti-Sr-O), designed to yield predictable release of strontium. The Ti-Sr-O functionalized surface is compared to a routinely used, commercially available surface (SLActive™) with respect to bone-to-implant contact (BIC%) and new bone formation (BF%) in two defined regions of interest (ROI-I and ROI-II, respectively). Materials and methods: Ti-Sr-O functionalized, SLActive, and Grade 4 titanium implants were inserted in the femoral condyle of adult male New Zealand White rabbits. The PVD magnetron-sputtered Ti-Sr-O surface coating was characterized using scanning electron microscopy (SEM) for morphology and coating thickness. Strontium release and mechanical stability of the coating, under simulated insertion conditions, were evaluated. Furthermore, histomorphometrical BIC and BF were carried out 2 weeks after insertion. Results: Histomorphometry revealed increased bone formation of Ti-Sr-O with significant differences compared to SLActive and Grade 4 titanium in both regions of interest, ROI-I and ROI-II, at 0–250 µm and 250–500 µm distance from the implant surfaces. Analogous results of bone-to-implant contact were observed for the two modified surfaces. Conclusion: The results show that a nanopatterned Ti-Sr-O functionalized titanium surface, with sustained release of strontium, increases peri-implant bone volume and could potentially contribute to enhancement of bone anchorage of osseointegrated implants.

Since strontium (Sr) is known for its anabolic and anticatabolic effect on bone, research has been focused on its potential impact on osseointegration. The objective of this study was to investigate the performance of nanotopographic implants with a Sr-functionalized titanium (Ti) coating (Ti–Sr–O) with respect to osseointegration in osteoporotic bone. The trial was designed to examine the effect of sustained-release characteristics of Sr in poor-quality bone. Three Ti–Sr–O groups, which differed from each other in coating thickness, Sr contents, and Sr release, were examined. These were prepared by a magnetron sputtering process and compared to uncoated grade 4 Ti. Composition, morphology, and mechanical stability of the coatings were analyzed, and Sr release data were gained from in vitro washout experiments. In vivo investigation was carried out in an osteoporotic rat model and analyzed histologically, 6 weeks and 12 weeks after implantation. Median values of bone-to-implant contact and new bone formation after 6 weeks were found to be 84.7% and 54.9% (best performing Sr group) as compared to 65.2% and 23.8% (grade 4 Ti reference), respectively. The 12-week observation period revealed 84.3% and 56.5% (best performing Sr group) and 81.3% and 39.4% (grade 4 Ti reference), respectively, for the same measurements. The increase in new bone formation was found to correlate with the amount of Sr released in vitro. The results indicate that sputtered nanostructured Ti–Sr–O coatings showed sustained release of Sr and accelerate osseointegration even in poor-quality bone, and thus, may have impact on practical applications for medical implants.

Cervical lymph node metastases in oral squamous cell carcinoma (OSCC) are key predictors of disease specific survival. It was therefore the aim of this study to evaluate how much imaging is minimally needed for reliable and efficient identification of cervical lymph node metastases. In this retrospective cross-sectional study, results (metastasis yes/no) of ultrasound (US), computed tomography (CT), magnetic resonance imaging (MRI), and positron emission tomography (PET) were compared to the final histopathological results of the corresponding neck dissection (ND) specimens (metastasis yes/no). A score was calculated to account for cervical lymph node size, shape, clustering, peripheral enhancement, hilus sign, architecture, blood flow, and central necrosis. Sensitivity and specificity were analyzed for each imaging technique separately. In 164 patients diagnosed with OSCC, 96 underwent uni- or bilateral ND (122 ND in total). One hundred percent sensitivity was achieved by CT+MRI, MRI+PET, US+CT+MRI, US+MRI+PET, CT+MRI+PET, and US+CT+MRI+PET. The highest specificity was realized by US with 79% (95% CI [0.698–0.890]). Specificity for CT+MRI and PET+MRI was 51% (95% CI [0.359–0.665]) and 70% (95% CI [0.416–0.984]), respectively. Regarding 100% sensitivity with acceptable specificity, the combination of CT+MRI or PET+MRI appeared to be suitable for staging cervical lymph nodes in primary OSCC.