Silk fibroin (SF)-based materials are exposed to both natural and artificial ultraviolet (UV) light during preparation or administration. However, the effects of UV irradiation on SF films prepared under different conditions have not yet been described in detail. In this study, four SF films with different molecular weight (MW) distribution were fabricated using SF solutions, which were prepared by dissolving degummed SF for 0.5–24 h. We observed UV (365 nm) irradiation on SF films induced the increase of yellowness and absorbance at 310 nm of SF films, indicating the formation of new photo-products and di-tyrosine bonds by photo-oxidation. Due to di-tyrosine cross-links between SF chains, UV-irradiated SF films were not fully dissociated in urea solution. In addition to formation of new products, UV reduced the crystallinity of SF films by breaking hydrogen bonds of β-sheet conformation. Unlike the UV-induced decomposition of physical interactions, UV did not affect the covalent bonds (i.e., peptide bonds). Through these experiments, we could expect that SF with higher MW was more susceptible and SF with lower MW was more resistant to UV-induced photo-oxidation and photo-degradation. These results provide useful information about UV-induced aging of SF-based materials under natural sunlight and UV irradiating conditions.

Mulberry fruits are rich sources of anthocyanins that exhibit beneficial biological activity. These anthocyanins become instable in an aqueous media, leading to their low bioavailability. In this study, a colloidal dispersion was produced by processing mulberry samples with hot-melt extrusion. In this process, hydrophilic polymer matrices were used to disperse the compound in an aqueous media. Mulberry samples were processed with hot-melt extrusion and in the presence of an ionization agent and sodium alginate to form mulberry-extrudate solid formulations. The particle size of mulberry-extrudate solid formulations decreased, while the total phenol content, the total anthocyanin content, and solubility increased. Fourier transform infrared spectroscopy (FT-IR) revealed that mulberry-extrudate solid formulations now contained new functional groups, such as –COOH group. We investigated whether mulberry-extrudate solid formulations had a positive impact on the stability of anthocyanins. The non-extrudate mulberry sample and mulberry-extrudate solid formulations were incubated with a simulated gastric fluid system and an intestinal fluid system. The number of released anthocyanins was determined with HPLC. We found that anthocyanins were released rapidly from non-extrudate mulberry extract. Mulberry-extrudate solid formulations contained a large number of available anthocyanins even after being incubated for 180 min in the intestinal fluid system. Thus, hot-melt extrusion enhanced water solubility and stability of anthocyanins with the prolonged release.

The aim of this study is to compare the functions of the physiologically active compounds of three types of mulberry leaf by cultivar, and to confirm the changes using hot-melt extrusion (HME−ML). The active components of mulberry leaf were analyzed using the HPLC system, and total phenolic content (TPC), total flavonoid content (TFC), and antioxidant activity were measured. Among the three varieties, the highest contents of rutin and isoquercetin were detected in Cheongil, of TPC in Cheongol, and of TFC in Cheongil. It was confirmed that this bio-accessibility was increased in HME−ML compared with the control. The DPPH radical scavenging activity of Cheongol showed greater antioxidant properties, and HME showed improvement in the antioxidant properties of all mulberry leaves. These results suggest that the application of HME technology can improve the biological activities of mulberry leaf.

Mulberry is a rich source of anthocyanins (ACNs) known to possess biological activities. However, these ACNs are unstable in high pH, heat, and aqueous environments with a low bioavailability. In this study, a colloidal dispersion was prepared by hot melt extrusion with proper excipients. In this process, a hydrophilic polymer matrix was used to confirm the stability of the compound in high pH, high temperature, and aqueous media. It was confirmed that the particle size and the polydispersity index value were reduced, thereby improving the solubility. In vitro release studies revealed that the extrudate had a sustained release compared to a non-extruded product. As a result of measuring changes of intestinal microorganisms (Lacticaseibacillus rhamnosus, Pediococcus pentosaceus, Escherichia coli, Enterococcus faecalis, and Staphylococcus aureus), contents of probiotics were found to be increased whereas contents of pathogenic microorganisms were decreased. Thus, hot-melt extrusion could enhance the stability of ACN with prolonged release. The processed formulation exhibited probiotic properties and antimicrobial activities against pathogenic intestinal microflora.

In this study, we investigated the anti-hypertensive properties of mulberry products by modulating the renin–angiotensin system (RAS). Comparative analysis showed that the ethyl acetate fractions, particularly from the Cheongil and Daeshim cultivars, contained the highest levels of polyphenols and flavonoids, with concentrations reaching 110 mg gallic acid equivalent (GE)/g and 471 mg catechin equivalent (CE)/g of extract, respectively. The ethyl acetate fraction showed superior angiotensin-converting enzyme (ACE) inhibitory activity, mainly because of the presence of the prenylated flavonoids kuwanon G and H. UPLC/Q-TOF-MS analysis identified kuwanon G and H as the primary active components, which significantly contributed to the pharmacological efficacy of the extract. In vivo testing of mice fed a high-salt diet showed that the ethyl acetate fraction substantially reduced the heart weight and lowered the serum renin and angiotensinogen levels by 34% and 25%, respectively, highlighting its potential to modulate the RAS. These results suggested that the ethyl acetate fraction of mulberry root bark is a promising candidate for the development of natural ACE inhibitors. This finding has significant implications for the management of hypertension through RAS regulation and the promotion of cardiovascular health in the functional food industry.

Recently, “mature” silkworms (MS) of Bombix mori have been considered a potential nutraceutical, with a number of health benefits reported for steamed and lyophilized MS powder (SMSP). However, no obesity-related effects have been reported for SMSP. In the present study, anti-obesity effects of SMSP were investigated in adult mice in vivo, aged 12 weeks at the onset of SMSP treatment, fed a normal diet (ND) and a high-fat diet (HFD), respectively, for 12 weeks. SMSP significantly suppressed body weight gain, intra-abdominal adipose tissue, and food efficiency in both ND-fed and HFD-fed adult mice. In addition, SMSP significantly decreased food intake and liver weight in HFD-fed mice, indicating that SMSP suppressed appetite and simultaneously reduced the conversion of feed into body weight in HFD-fed mice. SMSP also significantly lowered the serum levels of glucose, triglyceride, total cholesterol, low-density lipoprotein cholesterol, asparagine transaminase, alanine transaminase, and alkaline phosphatase. However, SMSP had no significant effect on the weights of the kidney, spleen, or thymus or the serum levels of blood urea nitrogen and creatinine. Taken together, the above results suggest that SMSP has potent anti-obesity effects and is safe for long-term use as a potential therapeutic and/or nutraceutical in both obese patients and non-obese individuals.